This work was supported by Technologico de Monterrey and the University of California at Irvine.

1. 3D Human Hair-derived Carbon Structure Fabrication
NOTE: Use personal protective equipment. Follow laboratory instructions to use the instruments and to work inside the laboratory.
<ol>
	<li>Prepare collected human hair by washing it with DI water and drying it with N2 gas.</li>
	<li>Arrange the hairs as desired, such as in parallel strands, cross over, with two hairs wound together, etc.</li>
	<li>Attach the hairs to a silicon substrate using SU8 or keep them directly in a ceramic boat.</li>
	<li>Place the hair-attached silicon substrate or boat into a furnace.</li>
	<li>Turn on the furnace and open the valve of an inert gas (N2) tank. 
	NOTE: The optimal gas flow rate is dependent upon the volume of the furnace tube. A 6 L/min flow rate was applied for a tube volume of 6 L. To establish a completely inert environment in the furnace tube, a gas flow rate 1.5 times higher than the optimal gas flow rate was applied for the first 15 min.</li>
	<li>Set the parameters, including maximum pyrolysis temperature, temperature ramp rate, and inert gas flow rate, and run the furnace.
	<ol>
		<li>For example, increase temperature from room temperature to 300 &#176;C at a 5 &#176;C/min ramp rate. Keep it at 300 &#176;C for 1 h for stabilization. Further increase the temperature to 900 &#176;C and maintain it for 1 h more for carbonization.</li>
		<li>Cool the furnace down to 300 &#176;C at a rate of 10 &#176;C/min and turn off the heater of the furnace, as the controlled cooling is not necessary after 300 &#176;C. Leave the samples in the furnace until the temperature reaches room temperature by N2 flow only.</li>
	</ol>
	</li>
	<li>Turn off the furnace and gas flow upon the completion of the pyrolysis process.</li>
	<li>Take the samples out of the furnace.</li>
</ol>
2. 3D Polymer Structure Fabrication: Photolithography
<ol>
	<li>Design a 2D layout of the desired 3D photoresist structure using an appropriate software package and prepare the printed mask (i.e., a polyethylene photofilm mask). 
	NOTE: A commercial service was used to get the design printed. The size of the mask generally depends on the design.</li>
	<li>In a clean laboratory facility, turn on two hot plates and set the temperatures to 65 &#176;C and 95 &#176;C, respectively.</li>
	<li>Switch on a spin coater and a vacuum pump. Ensure that the vacuum pump is connected through a tube to the spinner head.</li>
	<li>Set the parameters of the two-step spin, such as the spinning speed, ramp, and duration. For the first step, set the spinning speed to 500 rpm, the ramp to 100 rpm/s, and the spin time to 10 s to begin the spin cycle. For the next step, set the spinning speed to 1,000 rpm, the ramp to 100 rpm/s, and the spin time to 30 s to evenly spread the photoresist.</li>
	<li>Place a substrate (i.e., a 4 inch x 4 inch and 550 &#181;m &#177; 25 &#181;m-thick Si wafer with a 1 &#181;m-thick SiO2 layer) at the center of the holder.</li>
	<li>Deposit photosensitive polymer (i.e., SU8 photoresist) directly onto the center of the substrate. Use enough to cover the surface.</li>
	<li>Push the &#34;vacuum&#34; button to hold the substrate.</li>
	<li>Push the &#34;run&#34; button to coat the substrate with SU8 and to achieve a final thickness of 250 &#181;m.</li>
	<li>After the completion of spinning process, press the &#34;vacuum&#34; button again to release the coated substrate from the holder.</li>
	<li>Hold the coated substrate carefully using a tweezer to keep the surface smooth and clean. Transfer the substrate directly onto the hot plate at 65 &#176;C temperature for 6 min and then onto the hot plate at 95 &#176;C temperature for 40 min (soft bake). 
	NOTE: Baking at 65 &#176;C is required to ensure the slow evaporation of the solvent, resulting in the better coating and better adhesion to the substrate, while baking at 95 &#176;C further densifies the SU8.</li>
	<li>In the meantime, press the switch to turn on the UV-exposure system and set the time of exposure to &#34;12 s&#34; using the set button in the system. 
	NOTE: For a 250 &#181;m-thick SU8 layer, the exposure energy must be 360 mJ/cm2.</li>
	<li>Once the baking step (step 2.10) is completed, put the substrate into the UV-exposure system and place the printed side of a photomask (from step 2.1) onto it. Use the whole mask area to cover the coated substrate and press gently to ensure that there is no gap between the mask and substrate.</li>
	<li>Expose the SU8-coated substrate to UV radiation through the photomask using predefined UV settings.</li>
	<li>Heat the substrate again by placing it directly on the hotplate at 65 &#176;C for 5 min and at 95 &#176;C for 14 min for a post-exposure bake (PEB). 
	NOTE: The PEB increases the degree of cross-linking in the UV-exposed areas and makes the coating more resistant to solvents in the development step.</li>
	<li>Remove the unexposed photoresist regions by dipping the substrate in the dedicated developer solution, placed in a beaker, for 20 min. Continuously shake the solution (carefully) to ensure the complete removal of the un-exposed resist areas.</li>
	<li>Dry the developed structures by holding the substrate and blowing nitrogen or compressed air onto it.</li>
	<li>Inspect the wafer under a microscope with 50X magnification to compare the patterns transferred to the photoresist with the desired patterns.</li>
</ol>
3. 3D Carbon Structure Fabrication: Pyrolysis
<ol>
	<li>Place the samples prepared using photolithography (steps 2.1-2.17) inside a pressurized, open-ended tube furnace.</li>
	<li>Turn on the furnace and set the parameters for pyrolysis, as mentioned above in step 1. Repeat the process from step 1.6-1.8.</li>
	<li>Handle the samples carefully using tweezers and proceed to characterization.</li>
</ol>

<ol>
	<li>Wang, C., Jia, G., Taherabadi, L. H., Madou, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+novel+method+for+the+fabrication+of+high-aspect+ratio+C-MEMS+structures.">A novel method for the fabrication of high-aspect ratio C-MEMS structures.</a> J Microelectromech Syst. 14 (2), 348-358 (2005).</li><li>Jong, K. P. D., Geus, J. W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+nano&#64257;bers:+catalytic+synthesis+and+applications.">Carbon nano&#64257;bers: catalytic synthesis and applications.</a> Catal Rev Sci Eng. 42, 481-510 (2000).</li><li>Elrouby, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+applications+of+carbon+nanotube.">Electrochemical applications of carbon nanotube.</a> J Nano Adv Mat. 1 (1), 23-38 (2013).</li><li>Baughman, R. H., Zakhidov, A. A., Heer, W. A. D. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+nanotubes-the+route+toward+applications.">Carbon nanotubes-the route toward applications.</a> Science. 297, 787-792 (2002).</li><li>Kumar, R., Singh, R. K., Singh, D. P. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Natural+and+waste+hydrocarbon+precursors+for+the+synthesis+of+carbon+based+nanomaterials:+graphene+and+CNTs.">Natural and waste hydrocarbon precursors for the synthesis of carbon based nanomaterials: graphene and CNTs.</a> Renew Sustain Energy Rev. 58, 976-1006 (2016).</li><li>Afre, R. A., Soga, T., Jimbo, T., Kumar, M., Ando, Y., Sharon, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+nanotubes+by+spray+pyrolysis+of+turpentine+oil+at+different+temperatures+and+their+studies.">Carbon nanotubes by spray pyrolysis of turpentine oil at different temperatures and their studies.</a> Micropor Mesopor Mater. (1-3), 184-190 (2006).</li><li>Sharma, S., Kalita, G., Hirano, R., Hayashi, Y., Tanemura, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Influence+of+gas+composition+on+the+formation+of+graphene+domain+synthesized+from+camphor.">Influence of gas composition on the formation of graphene domain synthesized from camphor.</a> Mater Lett. 93, 258-262 (2013).</li><li>Ghosh, P., Afre, R. A., Soga, T., Jimbo, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+simple+method+of+producing+single-walled+carbon+nanotubes+from+a+natural+precursor:+eucalyptus+oil.">A simple method of producing single-walled carbon nanotubes from a natural precursor: eucalyptus oil.</a> Mater Lett. 61 (17), 3768-3770 (2007).</li><li>Kumar, R., Tiwari, R., Srivastava, O. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Scalable+synthesis+of+aligned+carbon+nanotubes+bundles+using+green+natural+precursor:+neem+oil.">Scalable synthesis of aligned carbon nanotubes bundles using green natural precursor: neem oil.</a> Nanoscale Res Lett. 6 (1), 92-97 (2011).</li><li>Liang, Y., Wu, D., Fu, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+microfibers+with+hierarchical+porous+structure+from+electrospun+fiber-like+natural+biopolymer.">Carbon microfibers with hierarchical porous structure from electrospun fiber-like natural biopolymer.</a> Sci Rep. 3, 1-5 (2013).</li><li>Gupta, A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Human+hair+"waste"+and+its+utilization:+gaps+and+possibilities.">Human hair "waste" and its utilization: gaps and possibilities.</a> J Waste Manag. 2014, 1-17 (2014).</li><li>Qian, W., Sun, F., Xu, Y., Qiu, L., Liu, C., Wang, S., Yan, F. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Human+hair-derived+carbon+flakes+for+electrochemical+supercapacitors.">Human hair-derived carbon flakes for electrochemical supercapacitors.</a> Energy Environ Sci. 7, 379-386 (2014).</li><li>Pramanick, B., Cadenas, L. B., Kim, D. M., Lee, W., Shim, Y. B., Martinez-Chapa, S. O., Madou, M. J., Hwang, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Human+hair-derived+hollow+carbon+microfibers+for+electrochemical+sensing.">Human hair-derived hollow carbon microfibers for electrochemical sensing.</a> Carbon. 107, 872-877 (2016).</li><li>Miura, N., Numaguchi, T., Yamada, A., Konagai, M., Shirakashi, J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Room+temperature+operation+of+amorphous+carbon-based+single-electron+transistors+fabricated+by+beam-induced+deposition+techniques.">Room temperature operation of amorphous carbon-based single-electron transistors fabricated by beam-induced deposition techniques.</a> Jpn J Appl Phys. 37 (2), L423-L425 (1998).</li><li>Irie, M., Endo, S., Wang, C. L., Ito, T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+and+properties+of+lateral+p-i-p+structures+using+single+crystalline+CVD+diamond+layers+for+high+electric+&#64257;eld+applications.">Fabrication and properties of lateral p-i-p structures using single crystalline CVD diamond layers for high electric &#64257;eld applications.</a> Diamond Rel Mater. 12, 1563-1568 (2003).</li><li>Tay, B. K., Sheeja, D., Yu, L. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=On+stress+reduction+of+tetrahedral+amorphous+carbon+&#64257;lms+for+moving+mechanical+assemblies.">On stress reduction of tetrahedral amorphous carbon &#64257;lms for moving mechanical assemblies.</a> Diamond Rel Mater. 12 (2), 185-194 (2003).</li><li>Kamath, R. R., Madou, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Three-dimensional+carbon+interdigitated+electrode+arrays+for+redox-amplification.">Three-dimensional carbon interdigitated electrode arrays for redox-amplification.</a> Anal Chem. 86 (6), 2963-2971 (2014).</li><li>Sharma, S., Khalajhedayati, A., Rupert, T. J., Madou, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=SU8+derived+glassy+carbon+for+lithium+ion+batteries.">SU8 derived glassy carbon for lithium ion batteries.</a> ECS Trans. 61 (7), 75-84 (2014).</li><li>Kim, D., Pramanick, B., Salazar, A., Tcho, I. -. W., Madou, M. J., Jung, E. S., Choi, Y. -. K., Hwang, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=3D+carbon+electrode+based+triboelectric+nanogenerator.">3D carbon electrode based triboelectric nanogenerator.</a> Adv Mater Technol. 1 (8), 1-7 (2016).</li><li>Duarte, R. M., Gorkin, R. A., Samra, K. B., Madou, M. J. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+integration+of+3D+carbon-electrode+dielectrophoresis+on+a+CD-like+centrifugal+microfluidic+platform.">The integration of 3D carbon-electrode dielectrophoresis on a CD-like centrifugal microfluidic platform.</a> Lab Chip. 10 (8), 1030-1043 (2010).</li><li>Mund, K., Richter, G., Weidlich, E., Fahlstrom, U. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Electrochemical+properties+of+platinum,+glassy+carbon,+and+pyrographite+as+stimulating+electrodes.">Electrochemical properties of platinum, glassy carbon, and pyrographite as stimulating electrodes.</a> Pacing Clin Electrophysiol. 9 (6), 1225-1229 (1986).</li><li>Xua, H., Malladi, K., Wang, C., Kulinsky, L., Song, M., Madou, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Carbon+post-microarrays+for+glucose+sensors.">Carbon post-microarrays for glucose sensors.</a> Biosens Bioelectron. 23 (11), 1637-1644 (2008).</li><li>Sharma, S., Madou, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Micro+and+nano+patterning+of+carbon+electrodes+for+bioMEMS.">Micro and nano patterning of carbon electrodes for bioMEMS.</a> Bioinspir Biomim Nanobiomat. 1, 252-265 (2012).</li><li>Pramanick, B., Martinez-Chapa, S. O., Madou, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fabrication+of+biocompatible+hollow+microneedles+using+the+C-MEMS+process+for+transdermal+drug+delivery.">Fabrication of biocompatible hollow microneedles using the C-MEMS process for transdermal drug delivery.</a> ECS Trans. 72 (1), 45-50 (2016).</li></ol>

The authors have nothing to disclose.

In this paper the methods for manufacturing a variety of carbon microstructures based on the pyrolysis of natural precursor materials or photo-patterned polymer structures were reported. The carbon materials resulting from both the traditional and non-conventional C-MEMS/C-NEMS processes are typically found to be glassy carbons. Glassy carbon is a widely used electrode material for electrochemistry and also for high-temperature applications. The microstructure of glassy carbon is composed of both crystalline and amorphous regions. Glassy carbon has high conductivity, good resistance to high temperatures, low density, low electrical resistance, and relatively high hardness and high resistance to chemical attack.
We proposed a simple and low-cost method to fabricate hollow glassy carbon microfibers from human hair and described their application to the electrochemical sensing of ascorbic acid and dopamine. The manufacturing of long, hollow, and electrically conductive carbon microfibers was possible with the low-cost, one-step thermal treatment of human hair, which is a waste material. A human hair composed of medulla, cortex, and cuticle, produced a hollow carbon fiber after pyrolysis. The medulla disappeared, whereas the cuticle and cortex combined together and create long, hollow carbon fibers. The unique anatomy of human hair, particularly its hollow structure after pyrolysis, is characterized by a significant increase in surface area, leading to their use in electrochemical sensing. For the working electrode modified with the hair-derived carbons, the peak potentials for dopamine and ascorbic acid were shifted towards more negative and positive values respectively. The surface of the hair-derived carbon is little negatively charged which attracs positively charged dopamine and therefore, the peak currents were increased for dopamine and decreased for ascorbic acid. As a result, human hair-derived hollow carbon microfibers could be useful to detect dopamine in the presence of ascorbic acid. A comparative study of electrochemical sensing performance of bare electrodes and modified electrodes (with hair-derived carbon and CNTs) has been carried out . The hair-derived carbon modified electrode shows better sensing performance than the unmodified electrode, but the CNT-coated electrodes showed the best performance for sensing dopamine and ascorbic acid in these experimental conditions, as was expected. The CNTs shows higher sensitivity due to their greater surface-area-to-volume ratio over hair-derived hollow carbon fibers. However, the major advantage of using hair-derived carbon microfibers over CNTs is the extremely low cost. Ease of fabrication of the hair-derived carbons also makes them dominate over CNTs. It is possible to enhance the sensing performance by further modification or functionalization of the human hairs before or after pyrolysis.
The shrinkage effect due to the pyrolysis is unavoidable, as non-carbon atoms detach from the carbon bonds at high temperatures, causing a substantial loss of mass. Before designing a desired structure, one should have a good estimate off the expected shrinkage of the patterned structure. Here, the shrinkage of the carbon structures fabricated using a conventional C-MEMS process, which includes two steps for the photo-patterning and pyrolysis of polymer structures, was studied. Five strucutres with different inner diameters (0, 30, 50, 75, and 100 &#181;m) were considered for the shrinkage study, whereas the outer diameter was kept constant at 150 &#181;m for all structures. The structures with inner diameters of 0, 30, 50, and 75 &#181;m showed more shrinkage on the outer diameter than the inner diameter after pyrolysis. In these cases, the outer surface areas were larger than the inner surface areas. Thus, the outer surfaces were dominant during the shrinking process, allowing more non-carbon atoms to leave the structures. In the structure with a 100 &#181;m inner diameter, where the inner surface area also made up a significant portion of the total surface area, the shrinkage ocurred at both the inner and the outer surfaces.
The parameters for pyrolysis, such as the pyrolysis time, the maximum pyrolysis temperature, and the atmospheric environment, significantly affect the properties of the carbon structure, such as the electrical conductivity, the chemical composition, the electrochemical property, etc. Ongoing research focuses on revealing the effects of pyrolysis conditions on the qualities and properties of carbon structures. In the case of conventional C-MEMS, carbon structures with diverse electrical and mechanical properties can also be fabricated, resulting in a wide variety of applications, by changing the photolithography conditions, such as the baking times, the baking temperature, the type of photoresist, and the additives. It is our belief that this research can provide substantial and useful information to researchers in the field of carbon structure nano/microfabrication for a variety of applications.

Carbon has many allotropes and, depending on the particular application, one of the following allotropes can be chosen: carbon nanotubes (CNTs), graphite, diamond, amorphous carbon, lonsdaleite, buckminsterfullerene (C60), fullerite (C540), fullerene (C70), and glassy carbon1,2,3,4. Glassy carbon is one of the most widely used allotropes because of its physical properties, including high isotropy. It also has the following properties: good electrical conductivity, low thermal expansion coefficient, and gas impermeability.
There has been a continuous search for carbon-rich precursor materials to obtain carbon structures. These precursors can be manmade materials or natural products that are available in particular shapes, and even include waste products. A wide variety of micro/nanostructures are formed via biological or environmental processes in nature, resulting in unique features that are extremely difficult to create using conventional manufacturing tools. As patterning took place naturally in this case, the synthesis of nanomaterials using natural and waste hydrocarbon precursors could be carried out using an easy, one-step process of thermal decomposition in an inert or vacuum atmosphere, called pyrolysis5. High-quality graphene, single-walled CNTs, multi-walled CNTs, and carbon dots have been produced by thermal decomposition or the pyrolysis of plant-derived precursors and wastes, including seeds, fibers, and oils, such as turpentine oil, sesame oil, neem oil (Azadirachta indica), eucalyptus oil, palm oil, and jatropha oil. Also, camphor products, tea-tree extracts, waste foods, insects, agro wastes, and food products have been utilized6,7,8,9 Recently, researchers have even used silk cocoons as a precursor material to prepare porous carbon microfibers10. Human hair, usually considered a waste material, was recently used by this team. It is made up of approximately 91% polypeptides, which contain more than 50% carbon; the rest are elements such as oxygen, hydrogen, nitrogen, and sulphur11. Hair also comes with several interesting properties, such as very slow degradation, high tensile strength, high thermal insulation, and high elastic recovery. Recently, it has been used to prepare carbon flakes employed in supercapacitors12 and to create hollow carbon microfibers for electrochemical sensing13.
The machining of a bulk carbon material to fabricate three-dimensional (3D) structures is a difficult task, as the material is very brittle. Focused ion beam14,15 or reactive ion etching16 may be useful in this context, but they are expensive and time-consuming processes. Carbon microelectromechanical system (C-MEMS) technology, which is based on the pyrolysis of patterned polymeric structures, represents a versatile alternative. In the past two decades, C-MEMS and carbon nanoelectromechanical systems (C-NEMS) have received much attention because of the simple and inexpensive fabrication steps involved. The conventional C-MEMS fabrication process is carried out in two steps: (i) patterning a polymer precursor (e.g., a photoresist) with photolithography and (ii) pyrolysis of the patterned structures. Ultraviolet (UV)-curable polymer precursors, such as SU8 photoresists, are often used to pattern structures based on photolithography. In general, the photolithography process includes steps for spin coating, soft bake, UV exposure, post bake, and development. In the case of C-MEMS; silicon; silicon dioxide; silicon nitride; quartz; and, more recently, sapphire have been used as substrates. The photo-patterned polymer structures are carbonized at a high temperature (800-1,100 &#176;C) in an oxygen-free environment. At those elevated temperatures in a vacuum or inert atmosphere, all of the non-carbon elements are removed, leaving only carbon. This technique allows for the attainment of high-quality, glassy carbon structures, which are very useful for many applications, including electrochemical sensing17, energy storage18, triboelectric nanogeneration19, and electrokinetic particle manipulation20. Also, the fabrication of 3D microstructures with high aspect ratios using C-MEMS has become relatively easy and has led to a wide variety of carbon electrodes applications18,21,22,23, often replacing noble metal electrodes.
In this work, the recent development of a simple and cost-effective way to fabricate hollow carbon microfibers from human hair using non-conventional C-MEMS technology13 is introduced. The conventional SU8 polymer-based C-MEMS process is also described here. Specifically, the fabrication procedure for high-aspect ratio solids and hollow SU8 structures is described24.

<table border="0" cellpadding="0" cellspacing="0" width="690">
	<tbody>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">SU8-2100</td>
			<td style="width:141px;">Microchem</td>
			<td style="width:167px;">Product number-Y1110750500L</td>
			<td style="width:167px;"></td>
		</tr>
		<tr height="63">
			<td height="63" style="height:63px;width:216px;">Spinner</td>
			<td style="width:141px;">Laurell Technologies Corporation</td>
			<td style="width:167px;">Model-WS650HZB-23NPP/UD3</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Hotplate</td>
			<td style="width:141px;">Torrey Pines Scientific</td>
			<td style="width:167px;">HS61</td>
			<td></td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">UV-exposer</td>
			<td style="width:141px;">Mercury Lamp, SYLVANIA</td>
			<td style="width:167px;">H44GS-100M, P/N-34-0054-01</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Photomask</td>
			<td style="width:141px;">CAD/Art</td>
			<td style="width:167px;"></td>
			<td>No number</td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Developer&#160;</td>
			<td style="width:141px;">Microchem</td>
			<td style="width:167px;">Y020100 4000L&#160;</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">DI water system</td>
			<td style="width:141px;">Milli Q</td>
			<td style="width:167px;">ZOOQOVOTO</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">IPA</td>
			<td style="width:141px;">CTR Sientific</td>
			<td style="width:167px;">CTR 01244</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">N2 gas</td>
			<td style="width:141px;">AOC Mexico</td>
			<td style="width:167px;"></td>
			<td>No number</td>
		</tr>
		<tr height="42">
			<td height="42" style="height:42px;width:216px;">Furnace</td>
			<td style="width:141px;">PEO 601, ATV Technologie GMBH</td>
			<td style="width:167px;">Model-PEO 601, Serial no.-195</td>
			<td></td>
		</tr>
		<tr height="21">
			<td height="21" style="height:21px;width:216px;">Si/SiO2</td>
			<td style="width:141px;">Noel Technologies</td>
			<td style="width:167px;"></td>
			<td></td>
		</tr>
	</tbody>
</table>

fabrication of 3d carbon microelectromechanical systems (c-mems)

A wide range of carbon sources are available in nature, with a variety of micro-/nanostructure configurations. Here, a novel technique to fabricate long and hollow glassy carbon microfibers derived from human hairs is introduced. The long and hollow carbon structures were made by the pyrolysis of human hair at 900 &#176;C in a N2 atmosphere. The morphology and chemical composition of natural and pyrolyzed human hairs were investigated using scanning electron microscopy (SEM) and electron-dispersive X-ray spectroscopy (EDX), respectively, to estimate the physical and chemical changes due to pyrolysis. Raman spectroscopy was used to confirm the glassy nature of the carbon microstructures. Pyrolyzed hair carbon was introduced to modify screen-printed carbon electrodes ; the modified electrodes were then applied to the electrochemical sensing of dopamine and ascorbic acid. Sensing performance of the modified sensors was improved as compared to the unmodified sensors. To obtain the desired carbon structure design, carbon micro-/nanoelectromechanical system (C-MEMS/C-NEMS) technology was developed. The most common C-MEMS/C-NEMS fabrication process consists of two steps: (i) the patterning of a carbon-rich base material, such as a photosensitive polymer, using photolithography; and (ii) carbonization through the pyrolysis of the patterned polymer in an oxygen-free environment. The C-MEMS/NEMS process has been widely used to develop microelectronic devices for various applications, including in micro-batteries, supercapacitors, glucose sensors, gas sensors, fuel cells, and triboelectric nanogenerators. Here, recent developments of a high-aspect ratio solid and hollow carbon microstructures with SU8 photoresists are discussed. The structural shrinkage during pyrolysis was investigated using confocal microscopy and SEM. Raman spectroscopy was used to confirm the crystallinity of the structure, and the atomic percentage of the elements present in the material before and after pyrolysis was measured using EDX.

A schematic of the fabrication process for human hair-derived hollow carbon microfibers is shown in Figure 1. The carbonized human hair was characterized using SEM to estimate the shrinkage. The hair diameter shrank from 82.88 &#177; 0.003 &#181;m to 31.42 &#177; 0.003 &#181;m due to the pyrolysis. Scanning electron microscopic (SEM) images of various patterns made using hair-derived carbon microfibers are shown in Figure 2. The atomic percentages of the elements present in the hair before and after pyrolysis are presented in Table 1. The human hair used in this research was (atomic percent) 66.57% carbon, 16.19% oxygen, 7.94% nitrogen, 9.14% sulphur, and a small percentage of minerals such as calcium. The atomic percentage of carbon and oxygen was found to be 80.84%, and 14.83% respectively after the pyrolysis. Raman spectroscopic analysis of the hair before and after pyrolysis was also performed as shown in Figure 3. Only two broad peaks corresponding to the D- and G-bands were found for the hair after pyrolysis. The ratio of the intensities of the D-band to the G-band in the hair-derived carbon fibers was calculated to be 0.99, indicating that the hair-derived fibers are mostly glassy carbon.
The hair-derived carbon fibers were applied to detect dopamine and ascorbic acid using an electrochemical sensor. A screen-printed carbon electrode was modified with the hair-derived carbon fibers and used as the working electrode of the sensor. A schematic diagram of the carbon electrodes for electrochemical sensing is shown in Figure 4a. Cyclic voltammograms of 100 &#181;M dopamine and 100 &#181;M ascorbic acid in a 0.1 M phosphate buffer solution of pH 7.4 are shown in Figure 4b and c, respectively. A bare carbon electrode, a carbon electrode modified with the hair-derived carbon, and a carbon electrode modified with the CNTs were used as the working electrode of the sensors to compare the performance to detect dopamine and ascorbic acid. The oxidation peaks for dopamine were measured at 333 mV for the bare carbon electrode, 266 mV for the carbon electrode modified with the hair derived carbon fibers, and 96 mV for the electrode modified with the CNTs. The oxidation peaks for ascorbic acid were observed at 414 mV, 455 mV, and 297 mV for those electrodes, respectively.
A schematic diagram of the conventional C-MEMS process, the photolithographic patterning of a polymer precursor and the subsequent pyrolysis, is shown in Figure 5. These fabricated structures were characterized using confocal microscopy and SEM to estimate the shrinkage due to pyrolysis. Five cylindrical structures of the same height (250 &#181;m) and outer diameter (150 &#181;m), but with various inner diameters (i.e., 0 (solid), 30, 50, 75, and 100 &#181;m (hollow)) were fabricated for this study. The geometric changes of the cylindrical structures due to pyrolysis were measured. The percentage of shrinkage was varied for different inner and outer diameter structures. When the inner diameter was 0 &#181;m (a solid microstructure), the outer diameter shrank around 35%. When the the inner diameters were 30, 50, and 75 &#181;m, the outer diameters and inner diameters shrank around 42% and 30 - 35%, respectively. In the case of a 100-&#181;m inner diameter, the inner diameter expanded 12%, rather than shrinking, and the outer diameter shrank only 15%. In Figure 6, the SEM images of solid and hollow carbon microstructures, of which the original inner diameters were 30, 40, and 75 &#181;m, are shown. 3D optical images of hollow microstructures before and after pyrolysis are also shown in Figure 7. All the microstructures shrank almost 30% in height (250 to 175 &#181;m) according to the confocal microscopic images.
<img alt="Figure 1" class="xfigimg" src="/files/ftp_upload/55649/55649fig1.jpg" /> 
Figure 1: Schematic Diagram of the Fabrication Process for Human Hair-derived Hollow Carbon Microfibers. Reproduced with permission from reference13. Copyright 2016, Elsevier Ltd. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" class="xfigimg" src="/files/ftp_upload/55649/55649fig2.jpg" /> 
Figure 2: SEM Images of Different Patterns of Hair-derived Carbon Microfibers. (a and b) Aligned straight carbon microfibers. Scale bar = 50 &#181;m. (c and d) A coiled carbon microfiber. Scale bars = 20 and 100 &#181;m, respectively. (e and f) A broken hollow carbon microfiber. Reproduced with permission from reference13. Copyright 2016, Elsevier Ltd. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" class="xfigimg" src="/files/ftp_upload/55649/55649fig3.jpg" /> 
Figure 3: Raman Spectra of Human Hair Before and After Pyrolysis. Reproduced with permission from reference13. Copyright 2016, Elsevier Ltd. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 4" class="xfigimg" src="/files/ftp_upload/55649/55649fig4.jpg" /> 
Figure 4: Electrochemical Sensing of Dopamine and Ascorbic Acid. (a) Schematic diagram of carbon electrodes for electrochemical sensing. Cyclic voltammograms of (b) 100 &#181;M dopamine and (c) 100 &#181;M ascorbic acid. Reproduced with permission from reference13. Copyright 2016, Elsevier Ltd. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig4large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 5" class="xfigimg" src="/files/ftp_upload/55649/55649fig5.jpg" /> 
Figure 5: A Schematic Diagram of the Conventional C-MEMS Process Based on Photolithography and pyrolysis. (a) Spin coating of photoresist, (b) UV-exposure, (c) development, and (d) pyrolysis. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig5large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 6" class="xfigimg" src="/files/ftp_upload/55649/55649fig6.jpg" /> 
Figure 6: Scanning Electron Microscopic Images of Carbon Microstructures Fabricated by the Conventional C-MEMS Process. (a) Solid and (b) hollow structures with various inner diameters. Scale bars = 500 &#181;m. Enlarged images for (c) the solid and the hollow structures, of which the inner diameters before pyrolysis were (d) 30, (e) 50, and (f) 75 &#181;m. Scale bars = 50 &#181;m. Reproduced with permission from reference24. Copyright 2016, The Electrochemical Society. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig6large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 7" class="xfigimg" src="/files/ftp_upload/55649/55649fig7.jpg" /> 
Figure 7: 3D Optical Images of Hollow Microstructures. (a) Before and (b) after pyrolysis. Reproduced with permission from refernce24. Copyright 2016, The Electrochemical Society. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/55649/55649fig7large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>Element</td>
			<td>Before pyrolysis</td>
			<td>After pyrolysis</td>
		</tr>
		<tr>
			<td></td>
			<td>Atomic %</td>
			<td>Atomic %</td>
		</tr>
		<tr>
			<td>Carbon</td>
			<td>66.57</td>
			<td>80.84</td>
		</tr>
		<tr>
			<td>Oxygen</td>
			<td>16.19</td>
			<td>14.83</td>
		</tr>
		<tr>
			<td>Nitrogen</td>
			<td>7.94</td>
			<td>0</td>
		</tr>
		<tr>
			<td>Sulfur</td>
			<td>9.14</td>
			<td>0.21</td>
		</tr>
		<tr>
			<td>Calcium</td>
			<td>0.16</td>
			<td>0.21</td>
		</tr>
		<tr>
			<td>Sodium</td>
			<td>0</td>
			<td>0.22</td>
		</tr>
		<tr>
			<td>Silicon</td>
			<td>1.82</td>
			<td>3.69</td>
		</tr>
	</tbody>
</table>
Table 1: Chemical Composition Analyzed by EDX for Human Hair Before and After Pyrolysis. Reproduced with permission from reference13. Copyright 2016, Elsevier Ltd.

Watch this Scientific Journal Video about Fabrication of 3D Carbon Microelectromechanical Systems C-MEMS at JoVE.com

Fabrication of 3D Carbon Microelectromechanical Systems C-MEMS

Long and hollow glassy carbon microfibers were fabricated based on the pyrolysis of a natural product, human hair. The two fabrication steps of carbon microelectromechanical and carbon nanoelectromechanical systems, or C-MEMS and C-NEMS, are: (i) photolithography of a carbon-rich polymer precursor and (ii) pyrolysis of the patterned polymer precursor.

Fabrication of 3D Carbon Microelectromechanical Systems (C-MEMS)

A wide range of carbon sources are available in nature, with a variety of micro-/nanostructure configurations. Here, a novel technique to fabricate long ...

fabrication-of-3d-carbon-microelectromechanical-systems-c-mems

Nanyang Technological University

Research

JoVE Journal

Engineering

12.0K Views.  Tecnologico de Monterrey. Long and hollow glassy carbon microfibers were fabricated based on the pyrolysis of a natural product, human hair. The two fabrication steps of carbon microelectromechanical and carbon nanoelectromechanical systems, or C-MEMS and C-NEMS, are: (i) photolithography of a carbon-rich polymer precursor and (ii) pyrolysis of the patterned polymer precursor. 

Video: Fabrication of 3D Carbon Microelectromechanical Systems C-MEMS

Fabrication, Densification, and Replica Molding of 3D Carbon Nanotube Microstructures

The introduction of new materials and processes to microfabrication has, in large part, enabled many important advances in microsystems, lab-on-a-chip devices, and their applications. In particular, capabilities for cost-effective fabrication of polymer microstructures were transformed by the advent of soft lithography and other micromolding techniques 1, 2, and this led a revolution in applications of microfabrication to biomedical engineering and biology. Nevertheless, it remains challenging to fabricate microstructures with well-defined nanoscale surface textures, and to fabricate arbitrary 3D shapes at the micro-scale. Robustness of master molds and maintenance of shape integrity is especially important to achieve high fidelity replication of complex structures and preserving their nanoscale surface texture. The combination of hierarchical textures, and heterogeneous shapes, is a profound challenge to existing microfabrication methods that largely rely upon top-down etching using fixed mask templates. On the other hand, the bottom-up synthesis of nanostructures such as nanotubes and nanowires can offer new capabilities to microfabrication, in particular by taking advantage of the collective self-organization of nanostructures, and local control of their growth behavior with respect to microfabricated patterns. 
Our goal is to introduce vertically aligned carbon nanotubes (CNTs), which we refer to as CNT "forests", as a new microfabrication material. We present details of a suite of related methods recently developed by our group: fabrication of CNT forest microstructures by thermal CVD from lithographically patterned catalyst thin films; self-directed elastocapillary densification of CNT microstructures; and replica molding of polymer microstructures using CNT composite master molds. In particular, our work shows that self-directed capillary densification ("capillary forming"), which is performed by condensation of a solvent onto the substrate with CNT microstructures, significantly increases the packing density of CNTs. This process enables directed transformation of vertical CNT microstructures into straight, inclined, and twisted shapes, which have robust mechanical properties exceeding those of typical microfabrication polymers. This in turn enables formation of nanocomposite CNT master molds by capillary-driven infiltration of polymers. The replica structures exhibit the anisotropic nanoscale texture of the aligned CNTs, and can have walls with sub-micron thickness and aspect ratios exceeding 50:1. Integration of CNT microstructures in fabrication offers further opportunity to exploit the electrical and thermal properties of CNTs, and diverse capabilities for chemical and biochemical functionalization 3.

We present methods for fabrication of patterned microstructures of vertically aligned carbon nanotubes (CNTs), and their use as master molds for production of polymer microstructures with organized nanoscale surface texture. The CNT forests are densified by condensation of solvent onto the substrate, which significantly increases their packing density and enables self-directed formation of 3D shapes.

The introduction of new materials and processes to microfabrication has, in large part, enabled many important advances in microsystems, lab-on-a-chip ...

High-resolution, High-speed, Three-dimensional Video Imaging with Digital Fringe Projection Techniques

Digital fringe projection (DFP) techniques provide dense 3D measurements of dynamically changing surfaces.&#160;Like the human eyes and brain, DFP uses triangulation between matching points in two views of the same scene at different angles to compute depth.&#160;However, unlike a stereo-based method, DFP uses a digital video projector to replace one of the cameras1. The projector rapidly projects a known sinusoidal pattern onto the subject, and the surface of the subject distorts these patterns in the camera&#8217;s field of view. Three distorted patterns (fringe images) from the camera can be used to compute the depth using triangulation.
Unlike other 3D measurement methods, DFP techniques lead to systems that tend to be faster, lower in equipment cost, more flexible, and easier to develop.&#160;DFP systems can also achieve the same measurement resolution as the camera.&#160;For this reason, DFP and other digital structured light techniques have recently been the focus of intense research (as summarized in1-5). Taking advantage of DFP, the graphics processing unit, and optimized algorithms, we have developed a system capable of 30&#160;Hz 3D video data acquisition, reconstruction, and display for over 300,000 measurement points per frame6,7.&#160;Binary defocusing DFP methods can achieve even greater speeds8.
Diverse applications can benefit from DFP techniques. Our collaborators have used our systems for facial function analysis9, facial animation10, cardiac mechanics studies11, and fluid surface measurements, but many other potential applications exist.&#160;This video will teach the fundamentals of DFP techniques and illustrate the design and operation of a binary defocusing DFP system.

This video describes the fundamentals of digital fringe projection techniques, which provide dense 3D measurements of dynamically changing surfaces.&#160;It also demonstrates the design and operation of a high-speed binary defocusing system based on these techniques.

Digital fringe projection (DFP) techniques provide dense 3D measurements of dynamically changing surfaces.&#160;Like the human eyes and brain, DFP uses ...

Fabrication of Spatially Confined Complex Oxides

Complex materials such as high Tc superconductors, multiferroics, and colossal magnetoresistors have electronic and magnetic properties that arise from the inherent strong electron correlations that reside within them. These materials can also possess electronic phase separation in which regions of vastly different resistive and magnetic behavior can coexist within a single crystal alloy material. By reducing the scale of these materials to length scales at and below the inherent size of the electronic domains, novel behaviors can be exposed. Because of this and the fact that spin-charge-lattice-orbital order parameters each involve correlation lengths, spatially reducing these materials for transport measurements is a critical step in understanding the fundamental physics that drives complex behaviors. These materials also offer great potential to become the next generation of electronic devices 1-3. Thus, the fabrication of low dimensional nano- or micro-structures is extremely important to achieve new functionality. This involves multiple controllable processes from high quality thin film growth to accurate electronic property characterization. Here, we present fabrication protocols of high quality microstructures for complex oxide manganite devices. Detailed descriptions and required equipment of thin film growth, photo-lithography, and wire-bonding are presented.

We describe the use of pulsed laser deposition (PLD), photolithography and wire-bonding techniques to create micrometer scale complex oxides devices. The PLD is utilized to grow epitaxial thin films. Photolithography and wire-bonding techniques are introduced to create practical devices for measurement purposes.

Complex materials such as high Tc superconductors, multiferroics, and colossal magnetoresistors have electronic and magnetic properties that arise from ...

Fabrication and Testing of Microfluidic Optomechanical Oscillators

Cavity optomechanics experiments that parametrically couple the phonon modes and photon modes have been investigated in various optical systems including microresonators. However, because of the increased acoustic radiative losses during direct liquid immersion of optomechanical devices, almost all published optomechanical experiments have been performed in solid phase. This paper discusses a recently introduced hollow microfluidic optomechanical resonator. Detailed methodology is provided to fabricate these ultra-high-Q microfluidic resonators, perform optomechanical testing, and measure radiation pressure-driven breathing mode and SBS-driven whispering gallery mode parametric vibrations. By confining liquids inside the capillary resonator, high mechanical- and optical- quality factors are simultaneously maintained.

Parametric optomechanical excitations have recently been experimentally demonstrated in microfluidic optomechanical resonators by means of optical radiation pressure and stimulated Brillouin scattering. This paper describes the fabrication of these microfluidic resonators along with methodologies for generating and verifying optomechanical oscillations.

Cavity optomechanics experiments that parametrically couple the phonon modes and photon modes have been investigated in various optical systems including ...

Fabrication of Low Temperature Carbon Nanotube Vertical Interconnects Compatible with Semiconductor Technology

We demonstrate a method for the low temperature growth (350 &#176;C) of vertically-aligned carbon nanotubes (CNT) bundles on electrically conductive thin-films. Due to the low growth temperature, the process allows integration with modern low-&#954; dielectrics and some flexible substrates. The process is compatible with standard semiconductor fabrication, and a method for the fabrication of electrical 4-point probe test structures for vertical interconnect test structures is presented. Using scanning electron microscopy the morphology of the CNT bundles is investigated, which demonstrates vertical alignment of the CNT and can be used to tune the CNT growth time. With Raman spectroscopy the crystallinity of the CNT is investigated. It was found that the CNT have many defects, due to the low growth temperature. The electrical current-voltage measurements of the test vertical interconnects displays a linear response, indicating good ohmic contact was achieved between the CNT bundle and the top and bottom metal electrodes. The obtained resistivities of the CNT bundle are among the average values in the literature, while a record-low CNT growth temperature was used.

A method for the growth of low temperature vertically-aligned carbon nanotubes, and the subsequent fabrication of vertical interconnect electrical test structures using semiconductor fabrication is presented.

We demonstrate a method for the low temperature growth (350 &#176;C) of vertically-aligned carbon nanotubes (CNT) bundles on electrically conductive ...

Fabrication and Characterization of Superconducting Resonators

Superconducting microwave resonators are of interest for a wide range of applications, including for their use as microwave kinetic inductance detectors (MKIDs) for the detection of faint astrophysical signatures, as well as for quantum computing applications and materials characterization. In this paper, procedures are presented for the fabrication and characterization of thin-film superconducting microwave resonators. The fabrication methodology allows for the realization of superconducting transmission-line resonators with features on both sides of an atomically smooth single-crystal silicon dielectric. This work describes the procedure for the installation of resonator devices into a cryogenic microwave testbed and for cool-down below the superconducting transition temperature. The set-up of the cryogenic microwave testbed allows one to do careful measurements of the complex microwave transmission of these resonator devices, enabling the extraction of the properties of the superconducting lines and dielectric substrate (e.g., internal quality factors, loss and kinetic inductance fractions), which are important for device design and performance.

Superconducting microwave resonators are of interest for detection of light, quantum computing applications and materials characterization. This work presents a detailed procedure for fabrication and characterization of superconducting microwave resonator scattering parameters.

Superconducting microwave resonators are of interest for a wide range of applications, including for their use as microwave kinetic inductance detectors ...

Two-way Valorization of Blast Furnace Slag: Synthesis of Precipitated Calcium Carbonate and Zeolitic Heavy Metal Adsorbent

The aim of this work is to present a zero-waste process for storing CO2 in a stable and benign mineral form while producing zeolitic minerals with sufficient heavy metal adsorption capacity. To this end, blast furnace slag, a residue from iron-making, is utilized as the starting material. Calcium is selectively extracted from the slag by leaching with acetic acid (2 M CH3COOH) as the extraction agent. The filtered leachate is subsequently physico-chemically purified and then carbonated to form precipitated calcium carbonate (PCC) of high purity (&lt;2 wt% non-calcium impurities, according to ICP-MS analysis). Sodium hydroxide is added to neutralize the regenerated acetate. The morphological properties of the resulting calcitic PCC are tuned for its potential application as a filler in papermaking. In parallel, the residual solids from the extraction stage are subjected to hydrothermal conversion in a caustic solution (2 M NaOH) that leads to the predominant formation of a particular zeolitic mineral phase (detected by XRD), namely analcime (NaAlSi2O6&#8729;H2O). Based on its ability to adsorb Ni2+, as reported from batch adsorption experiments and ICP-OES analysis, this product can potentially be used in wastewater treatment or for environmental remediation applications.

A protocol for the parallel production of precipitated calcium carbonate and zeolitic material from blast furnace slag via mineral carbonation and alkaline hydrothermal conversion, respectively, is presented. The performance of the zeolitic material towards nickel adsorption is tested.

The aim of this work is to present a zero-waste process for storing CO2 in a stable and benign mineral form while producing zeolitic minerals with ...

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia (YSZ) Scaffolds by In Situ Carbon Templating Xerogels

We demonstrate a method for the high temperature fabrication of porous, nanostructured yttria-stabilized-zirconia (YSZ, 8 mol% yttria - 92 mol% zirconia) scaffolds with tunable specific surface areas up to 80 m2&#183;g-1. An aqueous solution of a zirconium salt, yttrium salt, and glucose is mixed with propylene oxide (PO) to form a gel. The gel is dried under ambient conditions to form a xerogel. The xerogel is pressed into pellets and then sintered in an argon atmosphere. During sintering, a YSZ ceramic phase forms and the organic components decompose, leaving behind amorphous carbon. The carbon formed in situ serves as a hard template, preserving a high surface area YSZ nanomorphology at sintering temperature. The carbon is subsequently removed by oxidation in air at low temperature, resulting in a porous, nanostructured YSZ scaffold. The concentration of the carbon template and the final scaffold surface area can be systematically tuned by varying the glucose concentration in the gel synthesis. The carbon template concentration was quantified using thermogravimetric analysis (TGA), the surface area and pore size distribution was determined by physical adsorption measurements, and the morphology was characterized using scanning electron microscopy (SEM). Phase purity and crystallite size was determined using X-ray diffraction (XRD). This fabrication approach provides a novel, flexible platform for realizing unprecedented scaffold surface areas and nanomorphologies for ceramic-based electrochemical energy conversion applications, e.g. solid oxide fuel cell (SOFC) electrodes.

High Temperature Fabrication of Nanostructured Yttria-Stabilized-Zirconia YSZ Scaffolds by In Situ Carbon Templating Xerogels

A protocol for fabricating porous, nanostructured yttria-stabilized-zirconia (YSZ) scaffolds at temperatures between 1,000 &#176;C and 1,400 &#176;C is presented.

We demonstrate a method for the high temperature fabrication of porous, nanostructured yttria-stabilized-zirconia (YSZ, 8 mol% yttria - 92 mol% zirconia) ...

Production and Characterization of Vacuum Deposited Organic Light Emitting Diodes

A method for producing simple and efficient thermally-activated delayed fluorescence organic light-emitting diodes (OLEDs) based on guest-host or exciplex donor-acceptor emitters is presented. With a step-by-step procedure, readers will be able to repeat and produce OLED devices based on simple organic emitters. A patterning procedure allowing the creation of personalized indium tin oxide (ITO) shape is shown. This is followed by the evaporation of all layers, encapsulation and characterization of each individual device. The end goal is to present a procedure that will give the opportunity to repeat the information presented in cited publication but also using different compounds and structures in order to prepare efficient OLEDs.

A protocol for the production of simple structured organic light-emitting diodes (OLEDs) is presented.

A method for producing simple and efficient thermally-activated delayed fluorescence organic light-emitting diodes (OLEDs) based on guest-host or exciplex ...

Atmospheric Pressure Fabrication of Large-Sized Single-Layer Rectangular SnSe Flakes

Tin selenide (SnSe) belongs to the family of layered metal chalcogenide materials with a buckled structure like phosphorene, and has shown potential for applications in two-dimensional nanoelectronics devices. Although many methods to synthesize SnSe nanocrystals have been developed, a simple way to fabricate large-sized single-layer SnSe flakes remains a great challenge. Herein, we show the experimental method to directly grow large-sized single-layer rectangular SnSe flakes on commonly used SiO2/Si insulating substrates using a straightforward two-step fabrication method in an atmospheric pressure quartz tube furnace system. The single-layer rectangular SnSe flakes with an average thickness of ~6.8 &#197; and lateral dimensions of about 30 &#181;m &#215; 50 &#181;m were fabricated by a combination of vapor transport deposition technique and nitrogen etching route. We characterized the morphology, microstructure, and electrical properties of the rectangular SnSe flakes and obtained excellent crystallinity and good electronic properties. This article about the two-step fabrication method can help researchers grow other similar two-dimensional, large-sized, single-layer materials using an atmospheric pressure system.

A protocol is presented demonstrating a two-step fabrication technique to grow large-sized single-layer rectangular shaped SnSe flakes on low-cost SiO2/Si dielectrics wafers in an atmospheric pressure quartz tube furnace system.

Tin selenide (SnSe) belongs to the family of layered metal chalcogenide materials with a buckled structure like phosphorene, and has shown potential for ...