This work was financed through the Bristol Centre for Functional Nanomaterials, sponsored by the Engineering and Physical Sciences Research Council (EPSRC grant code EP/G036780/1).

Human mesenchymal stem cells (hMSC) were harvested from the proximal femur bone marrow of osteoarthritic patients undergoing total hip replacement surgery, in full accordance with Bristol Southmead Hospital Research Ethics Committee guidelines (reference #078/01) and after patient consent was obtained.
1. Magnetoferritin Synthesis and Purification
<ol>
	<li>General remarks
	<ol>
		<li>Perform magnetoferritin synthesis in a sealable, double-jacketed reaction vessel at 65 &#176;C under nitrogen atmosphere to restrict oxidation of the metal precursors. Inject metal salt solutions and hydrogen peroxide through access ports in the lid into the reaction vessel using a syringe pump.</li>
		<li>After magnetoferritin synthesis, purify the protein by anion-exchange chromatography (see section 1.4) to remove nanoparticles not enclosed in the protein cavity, followed by size-exclusion chromatography (see section 1.5) to isolate protein monomers. Determine protein concentration using a Bradford assay (see section 1.6).</li>
	</ol>
	</li>
	<li>Preparations prior to synthesis
	<ol>
		<li>Deoxygenate 500 ml of deionized water by placing a tube connected to a nitrogen gas cylinder in the water, sealing the vessel with cling film and bubbling through nitrogen gas for approximately 60 min.</li>
		<li>Heat a water bath connected to the double jacketed reaction vessel to 65 &#176;C. Add 75 ml of 50 mM 4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES) buffer (pH 8.6) into the reaction vessel, seal the vessel, and deoxygenate by bubbling nitrogen gas through the buffer solution for approximately 20 min. At the same time, stir the buffer solution using a magnetic stirrer.</li>
		<li>After deoxygenating the HEPES buffer solution, remove the tube supplying the nitrogen gas from the buffer and keep it suspended in the vessel to maintain a nitrogen atmosphere. Add apo-ferritin to achieve a final concentration of 3 mg/ml. Continue the magnetic stirring, but reduce the stirring speed if foaming occurs.</li>
		<li>Prepare a 25 mM stock solution of cobalt sulfate heptahydrate by dissolving 0.19 g in 50 ml of deoxygenated deionized water.</li>
		<li>Prepare a 25 mM solution of ammonium iron sulfate hexahydrate solution by dissolving 0.98 g in 100 ml of deoxygenated deionized water.</li>
		<li>Remove 2.5 ml of the ammonium iron sulfate hexahydrate solution and replace with 2.5 ml of the cobalt sulfate heptahydrate.</li>
		<li>Prepare an 8.33 mM solution of hydrogen peroxide in deoxygenated deionized water by first adding 965 &#956;l of a hydrogen peroxide solution (30% w/w) to 9 ml of deoxygenated deionized water, and then adding 1 ml of this sub-stock to 99 ml of deoxygenated deionized water.</li>
	</ol>
	</li>
	<li>Magnetoferritin synthesis
	<ol>
		<li>Inject 10.1 ml of both the iron-cobalt precursor and the hydrogen peroxide simultaneously into the apo-ferritin solution (magnetically stirred) at a flow rate of 0.15 ml/min using two syringe pump (total volume injected: 20.2 ml).</li>
		<li>During the injection period, deoxygenate another 500 ml of deionized water. 
		NOTE: The contents of the reaction vessel gradually adopt a dark brown color as the reaction proceeds.</li>
		<li>Shortly before completion of the first injection, prepare another 100 ml of iron-cobalt precursor and hydrogen peroxide solution using the freshly deoxygenated deionized water.</li>
		<li>Repeat the injection step described in 1.3.1 using freshly prepared solutions of iron-cobalt and hydrogen peroxide.</li>
		<li>During the injection period, deoxygenate another 500 ml of deionized water, and proceed as described in 1.3.3 and 1.3.4.</li>
		<li>After the third injection, leave the solution to mature for 15 min under stirring.</li>
		<li>Add 1.5 ml of a 1 M sodium citrate solution to the reaction vessel to chelate free metal ions in solution.</li>
		<li>Remove the solution from the reaction vessel into 50 ml centrifuge tubes, centrifuge for 30 min at 4,350 x g and pass the supernatant through a 0.22 &#181;m syringe filter. At this stage, the filtered supernatant can be stored at 4 &#176;C until purification.</li>
	</ol>
	</li>
	<li>Ion exchange chromatography
	<ol>
		<li>Load the sample onto a column (2.5 cm diameter, 20 cm long) containing a cationic matrix using a peristaltic pump at a flow rate of 10 ml/min.</li>
		<li>Wash the column with approximately 100 ml of running buffer (50 mM Tris(hydroxymethyl)aminomethane (Tris) buffer, pH 8.0) using a gradient pump at a flow rate of 10 ml/min.</li>
		<li>To elute the protein, wash the column at 10 ml/min with increasing concentrations of sodium chloride (NaCl) in Tris buffer: 150, 500 and 1,000 mM final NaCl concentration, 150 ml of each concentration.</li>
		<li>As the protein elutes at a NaCl concentration of 500 mM, collect it in 50 ml fractions using an automated fraction collector. 
		NOTE: For a detailed protocol of ion exchange chromatography consult previously published protocols.26</li>
	</ol>
	</li>
	<li>Size exclusion chromatography
	<ol>
		<li>Concentrate the 150 ml of magnetoferritin to a volume of approximately 2 ml using a 15 ml centrifugal filter unit followed by a 4 ml volume unit. Refer to the manufacturer&#39;s instructions of the centrifugal filter units (see material list) for a detailed protocol of this procedure.</li>
		<li>Load the concentrated sample onto a gel filtration column using an injection loop.</li>
		<li>Wash the column with running buffer (50 mM Tris buffer, pH 8.0, containing 150 mM NaCl) at a flow rate of 1.3 ml/min.</li>
		<li>Collect 6 ml fractions using an automated fraction collector. Protein monomers elute last. At this point, purified magnetoferritin can be stored at 4 &#176;C until cationization. 
		NOTE: For a detailed protocol of size exclusion chromatography using a gel filtration column consult previously published protocols.27</li>
	</ol>
	</li>
	<li>Determining protein concentration
	<ol>
		<li>Prepare ferritin standards of 0.06, 0.125, 0.25, 0.5 and 1 mg/ml in 50 mM Tris buffer using commercially available horse spleen ferritin. 
		NOTE: The protein concentration of commercially available ferritin is stated on the bottle. If not, contact the supplier for this information.</li>
		<li>Dilute magnetoferritin samples of unknown concentration in 50 mM Tris buffer until the color of the solution approximately matches the color of the 0.5 mg/ml standard. Make a note of the dilution factor.</li>
		<li>Add 10 &#956;l of each standard and magnetoferritin sample in triplicate into wells of a 96 well plate.</li>
		<li>Add 200 &#956;l of ready-made Bradford reagent to each well (refer to materials list for Bradford assay reagent details).</li>
		<li>Incubate at room temperature for 8 minutes.</li>
		<li>Measure the absorbance at &#955; = 595 nm using a microplate reader.</li>
		<li>Plot the mean absorbance of the ferritin standards as a function of protein concentration and use the slope and intercept of the linear fit to calculate the concentration of the magnetoferritin sample. 
		NOTE: Take into account the dilution factor that was used to adjust the magnetoferritin sample to the standard curve.</li>
	</ol>
	</li>
</ol>
2. Magnetoferritin Cationization
<ol>
	<li>General remarks 
	NOTE: For magnetoferritin cationization, N,N-dimethyl-1,3-propanediamine (DMPA) was coupled to aspartic and glutamic acid residues on the MF surface using N-(3-dimethylaminopropyl)-N&#39;-ethylcarbodiimide hydrochloride (EDC).
	<ol>
		<li>Carry out the reaction at room temperature under stirring. The protocol given below is for the cationization of 10 mg of magnetoferritin in a total volume of 5 ml (protein concentration 2 mg/ml). However, scale up or down by keeping the protein:DMPA:EDC ratios consistent, as well as the volumes of the buffer and magnetoferritin solution.</li>
		<li>Prior to the cationization reaction, dialyze the magnetoferritin samples into 50 mM phosphate buffer (pH 7) containing 50 mM NaCl. This is important to remove Tris elution buffer and avoid unwanted reactions between the Tris amine and the EDC-activated carboxylic acid residues. Determine the protein concentration after dialysis and adjust it to 4 mg/ml prior to cationization.</li>
	</ol>
	</li>
	<li>Cationization protocol
	<ol>
		<li>Weigh out 374 mg of DMPA and dissolve in 2.5 ml of 200 mM 2-(N-morpholino)ethanesulfonic acid (MES) buffer.</li>
		<li>Adjust the solution pH to approximately 7 using concentrated (6 M) hydrochloric acid (HCl). 
		CAUTION: Perform this step in a fume hood, as addition of the acid to DMPA releases toxic fumes!</li>
		<li>Add 2.5 ml of magnetoferritin solution at 4 mg/ml (final concentration of MES is 100 mM, final concentration of magnetoferritin is 2 mg/ml, total amount of protein is 10 mg).</li>
		<li>Add a magnetic stirrer and stir for 2 hr to equilibrate.</li>
		<li>Carefully adjust the solution to pH 5.0 using 1 M HCl.</li>
		<li>Add 141 mg of EDC powder to the DMPA/magnetoferritin solution.</li>
		<li>Continue stirring for 3.5 hr.</li>
		<li>Filter the solution through a 0.22 &#181;m syringe filter to remove any precipitates.</li>
		<li>Add the solution to dialysis tubing with a 12-14 kDa molecular weight cut-off and dialyze against 4 L of 50 mM phosphate buffer (pH 7) containing 50 mM NaCl for 2 days at 4 &#176;C, replacing the dialysis buffer at least three times during that period. 
		NOTE: At this point, cationized magnetoferritin can be stored at 4 &#176;C until further use.</li>
	</ol>
	</li>
</ol>
3. Human Mesenchymal Stem Cell Labeling with Cationized Magnetoferritin
<ol>
	<li>General remarks
	<ol>
		<li>Perform all cell culture using class II laminar flow cabinets and humidified incubators at 37 &#176;C and 5% carbon dioxide atmosphere.</li>
		<li>Culture cells as monolayers using 175 cm2 flasks and 20 ml of culture medium, which was replenished every 3 - 4 days. Culture medium consisted of Dulbecco&#39;s Modified Eagle&#39;s Medium (DMEM), containing 1,000 mg/L glucose, 10% (v/v) fetal bovine serum, 1% (v/v) penicillin/streptomycin solution, 1% (v/v) L-alanyl-L-glutamine solution and 5 ng/ml freshly supplemented human fibroblast growth factor.</li>
	</ol>
	</li>
	<li>Magnetic labeling of hMSC with cationized magnetoferritin
	<ol>
		<li>Seed 150,000 hMSCs into 25 cm2 flasks and leave to adhere overnight at 37 &#176;C.</li>
		<li>Filter sterilize cationized magnetoferritin through a 0.22 &#181;m syringe filter and determine the protein concentration.</li>
		<li>Keeping sterile conditions, prepare a 0.5 &#956;M solution of cationized magnetoferritin in phosphate buffered saline (PBS). Keep capped in a sterile culture hood until use.</li>
		<li>Wash the plated cells with 2 ml of room temperature PBS.</li>
		<li>Add 1 ml of the sterilized cationized magnetoferritin solution to the plated cells and incubate for the desired time period (1 min to 1 hr).</li>
		<li>Wash cells with PBS, and then harvest cells by adding 0.5 ml of trypsin/ethylenediaminetetraacetic acid (EDTA) and incubating at 37 &#176;C for 5 min.</li>
		<li>Add 1 ml of culture medium to inactivate the trypsin/EDTA, transfer the solution to a 15 ml centrifuge tube and centrifuge for 5 min at 524 x g.</li>
		<li>Discard the supernatant and re-suspend the cell pellet in 0.5 ml magnetic separation buffer, consisting of 0.5% (w/v) fetal bovine serum and 2 mM EDTA in PBS.</li>
	</ol>
	</li>
	<li>Magnetic cell separation
	<ol>
		<li>Attach the magnet to the multi stand, and add a magnetic separation column to the magnet. Place a pre-separation filter on the column.</li>
		<li>Place 0.5 ml of magnetic separation buffer in the pre-separation filter and let it run through both the filter and the column to wash and wet them.</li>
		<li>Place a 15 ml centrifuge tube under the column.</li>
		<li>Add 0.5 ml of the cell suspension in the filter reservoir of the magnetic separation column.</li>
		<li>When the reservoir is empty, add 0.5 ml of magnetic separation buffer.</li>
		<li>When the reservoir is empty, add further 0.5 ml of magnetic separation buffer.</li>
		<li>Repeat one more time (the total volume of magnetic separation buffer used for washing should be 1.5 ml). This wash step elutes all non-magnetized cells from the column (non-magnetized cell fraction).</li>
		<li>Remove the column from the magnet and place it in a fresh 15 ml centrifuge tube. Remove filter from the column reservoir.</li>
		<li>Add 1 ml of magnetic separation buffer to the reservoir and immediately push through the column using the plunger supplied by the manufacturer. This elutes the magnetized cells from the column into the centrifuge tube (magnetized cell fraction).</li>
		<li>Centrifuge both tubes for 5 min at 524 x g.</li>
		<li>Discard the supernatant and re-suspend the cell pellets in 0.3 ml PBS.</li>
		<li>Count the number of cells numbers in each fraction using a hemocytometer.</li>
		<li>Determine the fraction of magnetized cells, M(%), using the following equation: 
		<img alt="Equation" src="/files/ftp_upload/54785/54785eq1.jpg" />&#160; 
		where n(M) is the number of cells in the magnetized fraction and n(M+NM) is the sum of the number of cells in the magnetized and non-magnetized fractions.</li>
	</ol>
	</li>
	<li>Preparing hMSCs labeled with cationized magnetoferritin for iron quantification using inductively coupled plasma optical emission spectroscopy (ICP-OES) 
	NOTE: The protocol may need to be adapted for other ICP-OES instruments. It is advisable to consult with the responsible technician.
	<ol>
		<li>Centrifuge a known number of cells for 5 min at 524 x g.</li>
		<li>Remove the PBS supernatant and add 0.25 ml of 50% (v/v) nitric acid.</li>
		<li>Vortex mix the acidified cell suspension.</li>
		<li>Incubate at room temperature overnight.</li>
		<li>Add 4.75 ml of distilled water to each sample and vortex mix.</li>
		<li>Analyze with ICP-OES.28</li>
		<li>Normalize the measured iron content to the number of cells to determine a value for cellular iron content.</li>
	</ol>
	</li>
</ol>

<ol>
	<li>Gupta, A. K., Gupta, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthesis+and+surface+engineering+of+iron+oxide+nanoparticles+for+biomedical+applications.">Synthesis and surface engineering of iron oxide nanoparticles for biomedical applications.</a> Biomaterials. 26 (18), 3995-4021 (2005).</li><li>Decuzzi, P., Ferrari, M. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=The+role+of+specific+and+non-specific+interactions+in+receptor-mediated+endocytosis+of+nanoparticles.">The role of specific and non-specific interactions in receptor-mediated endocytosis of nanoparticles.</a> Biomaterials. 28 (18), 2915-2922 (2007).</li><li>Cunningham, C. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Positive+contrast+magnetic+resonance+imaging+of+cells+labeled+with+magnetic+nanoparticles.">Positive contrast magnetic resonance imaging of cells labeled with magnetic nanoparticles.</a> Magn. Reson. Med. 53 (5), 999-1005 (2005).</li><li>Song, H. T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Surface+modulation+of+magnetic+nanocrystals+in+the+development+of+highly+efficient+magnetic+resonance+probes+for+intracellular+labeling.">Surface modulation of magnetic nanocrystals in the development of highly efficient magnetic resonance probes for intracellular labeling.</a> J. Am. Chem. Soc. 127 (28), 9992-9993 (2005).</li><li>Daldrup-Link, H. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Targeting+of+hematopoietic+progenitor+cells+with+MR+contrast+agents.">Targeting of hematopoietic progenitor cells with MR contrast agents.</a> Radiology. 228 (3), 760-767 (2003).</li><li>Singh, N., Jenkins, G. J., Asadi, R., Doak, S. H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Potential+toxicity+of+superparamagnetic+iron+oxide+nanoparticles+(SPION).">Potential toxicity of superparamagnetic iron oxide nanoparticles (SPION).</a> Nano Rev. 1, (2010).</li><li>Dodd, S. J., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Detection+of+single+mammalian+cells+by+high-resolution+magnetic+resonance+imaging.">Detection of single mammalian cells by high-resolution magnetic resonance imaging.</a> Biophys. J. 76 (1), 103-109 (1999).</li><li>Ahrens, E. T., Feili-Hariri, M., Xu, H., Genove, G., Morel, P. A. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Receptor-mediated+endocytosis+of+iron-oxide+particles+provides+efficient+labeling+of+dendritic+cells+for+in+vivo+MR+imaging.">Receptor-mediated endocytosis of iron-oxide particles provides efficient labeling of dendritic cells for in vivo MR imaging.</a> Magn. Reson. Med. 49 (6), 1006-1013 (2003).</li><li>Arbab, A. S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Efficient+magnetic+cell+labeling+with+protamine+sulfate+complexed+to+ferumoxides+for+cellular+MRI.">Efficient magnetic cell labeling with protamine sulfate complexed to ferumoxides for cellular MRI.</a> Blood. 104 (4), 1217-1223 (2004).</li><li>Bulte, J. W. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Magnetodendrimers+allow+endosomal+magnetic+labeling+and+in+vivo+tracking+of+stem+cells.">Magnetodendrimers allow endosomal magnetic labeling and in vivo tracking of stem cells.</a> Nat. Biotechnol. 19 (12), 1141-1147 (2001).</li><li>Josephson, L., Tung, C. H., Moore, A., Weissleder, R. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-efficiency+intracellular+magnetic+labeling+with+novel+superparamagnetic-tat+peptide+conjugates.">High-efficiency intracellular magnetic labeling with novel superparamagnetic-tat peptide conjugates.</a> Bioconjugate Chem. 10 (2), 186-191 (1999).</li><li>Lewin, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Tat+peptide-derivatized+magnetic+nanoparticles+allow+in+vivo+tracking+and+recovery+of+progenitor+cells.">Tat peptide-derivatized magnetic nanoparticles allow in vivo tracking and recovery of progenitor cells.</a> Nat. Biotechnol. 18 (4), 410-414 (2000).</li><li>Hunter, A. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Molecular+hurdles+in+polyfectin+design+and+mechanistic+background+to+polycation+induced+cytotoxicity.">Molecular hurdles in polyfectin design and mechanistic background to polycation induced cytotoxicity.</a> Adv. Drug Delivery Rev. 58 (14), 1523-1531 (2006).</li><li>Montet-Abou, K., Montet, X., Weissleder, R., Josephson, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cell+internalization+of+magnetic+nanoparticles+using+transfection+agents.">Cell internalization of magnetic nanoparticles using transfection agents.</a> Mol. Imaging. 6 (1), 1-9 (2007).</li><li>Correia Carreira, ., S, , et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultra-fast+stem+cell+labelling+using+cationised+magnetoferritin.">Ultra-fast stem cell labelling using cationised magnetoferritin.</a> Nanoscale. 8 (14), 7474-7483 (2016).</li><li>Meldrum, F. C., Heywood, B. R., Mann, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Magnetoferritin:+in+vitro+synthesis+of+a+novel+magnetic+protein.">Magnetoferritin: in vitro synthesis of a novel magnetic protein.</a> Science. 257 (5069), 522-523 (1992).</li><li>Klem, M. T., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Synthetic+control+over+magnetic+moment+and+exchange+bias+in+all-oxide+materials+encapsulated+within+a+spherical+protein+cage.">Synthetic control over magnetic moment and exchange bias in all-oxide materials encapsulated within a spherical protein cage.</a> J. Am. Chem. Soc. 129 (1), 197-201 (2007).</li><li>Okuda, M., Eloi, J. C., Sarua, A., Jones, S. E. W., Schwarzacher, W. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Energy+barrier+distribution+for+dispersed+mixed+oxide+magnetic+nanoparticles.">Energy barrier distribution for dispersed mixed oxide magnetic nanoparticles.</a> J. Appl. Phys. 111 (7), (2012).</li><li>Uchida, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=A+human+ferritin+iron+oxide+nano-composite+magnetic+resonance+contrast+agent.">A human ferritin iron oxide nano-composite magnetic resonance contrast agent.</a> Magn. Reson. Med. 60 (5), 1073-1081 (2008).</li><li>Danon, D., Skutelsk E, M. a. r. i. k. o. v. s. Y., Goldstei, L. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Use+of+Cationized+Ferritin+as+a+Label+of+Negative+Charges+on+Cell+Surfaces.">Use of Cationized Ferritin as a Label of Negative Charges on Cell Surfaces.</a> J. Ultrastruc. Res. 38 (5-6), 500-510 (1972).</li><li>Valero, E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Magnetic+Nanoparticles-Templated+Assembly+of+Protein+Subunits:+A+New+Platform+for+Carbohydrate-Based+MRI+Nanoprobes.">Magnetic Nanoparticles-Templated Assembly of Protein Subunits: A New Platform for Carbohydrate-Based MRI Nanoprobes.</a> J. Am. Chem. Soc. 133 (13), 4889-4895 (2011).</li><li>Zborowski, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Immunomagnetic+isolation+of+magnetoferritin-labeled+cells+in+a+modified+ferrograph.">Immunomagnetic isolation of magnetoferritin-labeled cells in a modified ferrograph.</a> Cytometry. 24 (3), 251-259 (1996).</li><li>Ikezoe, Y., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Growth+of+Giant+Two-Dimensional+Crystal+of+Protein+Molecules+from+a+Three-Phase+Contact+Line.">Growth of Giant Two-Dimensional Crystal of Protein Molecules from a Three-Phase Contact Line.</a> Langmuir. 24 (22), 12836-12841 (2008).</li><li>Uchida, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Targeting+of+cancer+cells+with+ferrimagnetic+ferritin+cage+nanoparticles.">Targeting of cancer cells with ferrimagnetic ferritin cage nanoparticles.</a> J. Am. Chem. Soc. 128 (51), 16626-16633 (2006).</li><li>Yamashita, K., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Selective+nanoscale+positioning+of+ferritin+and+nanoparticles+by+means+of+target-specific+peptides.">Selective nanoscale positioning of ferritin and nanoparticles by means of target-specific peptides.</a> Small. 2 (10), 1148-1152 (2006).</li><li>Williams, A., Frasca, V., Coligan, J. E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=UNIT+8.2+Ion-Exchange+Chromatography.">UNIT 8.2 Ion-Exchange Chromatography.</a> Current Protocols in Protein Science. , (2001).</li><li>Hagel, L., et al., Coligan, J. E., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=UNIT+8.3+Gel-Filtration+Chromatography.">UNIT 8.3 Gel-Filtration Chromatography.</a> Current Protocols in Protein Science. , (2001).</li><li>Hou, X., Jones, B. T. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Inductively+coupled+plasma-optical+emission+spectrometry.">Inductively coupled plasma-optical emission spectrometry.</a> In Encyclopedia of Analytical Chemistry. Meyers, R.A. ed. , 1 (2000).</li><li>Correia Carreira, S., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Ultra-fast+stem+cell+labelling+using+cationised+magnetoferritin.">Ultra-fast stem cell labelling using cationised magnetoferritin.</a> Nanoscale. , (2016).</li><li>Simon, G. H., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=T1+and+T2+relaxivity+of+intracellular+and+extracellular+USPIO+at+1.5+T+and+3T+clinical+MR+scanning.">T1 and T2 relaxivity of intracellular and extracellular USPIO at 1.5 T and 3T clinical MR scanning.</a> Eur. J. Radiol. 16 (3), 738-745 (2006).</li><li>Jubb, A. M., Allen, H. C. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Vibrational+Spectroscopic+Characterization+of+Hematite,+Maghemite,+and+Magnetite+Thin+Films+Produced+by+Vapor+Deposition.">Vibrational Spectroscopic Characterization of Hematite, Maghemite, and Magnetite Thin Films Produced by Vapor Deposition.</a> ACS Appl. Mater. Interfaces. 2 (10), 2804-2812 (2010).</li><li>Wang, Z. W., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=High-pressure+x-ray+diffraction+and+Raman+spectroscopic+studies+of+the+tetragonal+spinel+CoFe2O4.">High-pressure x-ray diffraction and Raman spectroscopic studies of the tetragonal spinel CoFe2O4.</a> Phys. Rev. B. 68 (9), (2003).</li><li>Wong, K. K., Douglas, T., Gider, S., Awschalom, D. D., Mann, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Biomimetic+synthesis+and+characterization+of+magnetic+proteins+(magnetoferritin).">Biomimetic synthesis and characterization of magnetic proteins (magnetoferritin).</a> Chem. Mater. 10 (1), 279-285 (1998).</li><li>Okuda, M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Fe3O4+nanoparticles:+protein-mediated+crystalline+magnetic+superstructures.">Fe3O4 nanoparticles: protein-mediated crystalline magnetic superstructures.</a> Nanotechnology. 23 (41), 415601 (2012).</li><li>Perriman, A. W., C&#246;lfen, H., Hughes, R. W., Barrie, C. L., Mann, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Solvent-Free+Protein+Liquids+and+Liquid+Crystals.">Solvent-Free Protein Liquids and Liquid Crystals.</a> Angew. Chem. Int. Ed. 48 (34), 6242-6246 (2009).</li><li>Billotey, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=T-cell+homing+to+the+pancreas+in+autoimmune+mouse+models+of+diabetes:+in+vivo+MR+imaging.">T-cell homing to the pancreas in autoimmune mouse models of diabetes: in vivo MR imaging.</a> Radiology. 236 (2), 579-587 (2005).</li><li>Smirnov, P., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=In+vivo+cellular+imaging+of+lymphocyte+trafficking+by+MRI:+a+tumor+model+approach+to+cell-based+anticancer+therapy.">In vivo cellular imaging of lymphocyte trafficking by MRI: a tumor model approach to cell-based anticancer therapy.</a> Magn. Reson. Med. 56 (3), 498-508 (2006).</li><li>Wilhelm, C., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Magnetic+control+of+vascular+network+formation+with+magnetically+labeled+endothelial+progenitor+cells.">Magnetic control of vascular network formation with magnetically labeled endothelial progenitor cells.</a> Biomaterials. 28 (26), 3797-3806 (2007).</li><li>MacLean, I., Sanders, E. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Cationized+ferritin+and+phosvitin+uptake+by+coated+vesicles+of+the+early+chick+embryo.">Cationized ferritin and phosvitin uptake by coated vesicles of the early chick embryo.</a> Anat. Embryol. 166 (3), 385-397 (1983).</li><li>Van Deurs, B., Nilausen, K., Faergeman, O., Meinertz, H. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Coated+pits+and+pinocytosis+of+cationized+ferritin+in+human+skin+fibroblasts.">Coated pits and pinocytosis of cationized ferritin in human skin fibroblasts.</a> Eur. J. Cell Biol. 27 (2), 270-278 (1982).</li><li>Xing, R. M., et al. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Characterization+and+cellular+uptake+of+platinum+anticancer+drugs+encapsulated+in+apoferritin.">Characterization and cellular uptake of platinum anticancer drugs encapsulated in apoferritin.</a> J Inorg Biochem. 103 (7), 1039-1044 (2009).</li><li>Wong, K. K., Mann, S. <a target="_blank" href="http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed&cmd=Search&doptcmdl=Citation&defaultField=Title+Word&term=Biomimetic+synthesis+of+cadmium+sulfide-ferritin+nanocomposites.">Biomimetic synthesis of cadmium sulfide-ferritin nanocomposites.</a> Adv. Mater. 8 (11), 928-932 (1996).</li></ol>

The authors have nothing to disclose.

TEM of magnetoferritin samples stained with aurothioglucose revealed the successful mineralization of nanoparticles inside the protein cage. Electron diffraction and Raman analysis of the nanoparticle core indicated the presence of a cobalt ferrite, indicating successful doping of the nanoparticle core with cobalt. This demonstrates that mixed-oxide nanoparticles can successfully be mineralized within the apo-ferritin cavity. Furthermore, we have shown previously that cobalt doping can be varied by altering the amount of cobalt precursor added to the reaction mixture, which enables tuning of the magnetic properties.18
Magnetoferritin synthesis can be performed in a variety of vessels, as long as they are tightly sealable and have access ports through which reactants can be introduced (e.g., a three-neck round bottom flask). The reaction temperature should be maintained at 65 &#176;C either by placing the vessel in a water/oil bath or using a double-jacketed vessel. Here, we used a double-jacketed electrochemical cell setup to perform the synthesis. To guarantee successful synthesis, maintaining the correct pH and avoiding oxygen contamination of the aqueous solutions is crucial. Metal salt solutions should always be prepared freshly prior to use rather than in advance. Furthermore, commercial apoferritin solutions can vary in quality and affect synthesis outcome (e.g., size of nanoparticle core mineralized). It can help to dialyze the apoferritin solution into 50 mM HEPES buffer (pH 8.6) prior to synthesis to remove any residual reducing agent used by the manufacturer. It is useful to make a note of the batch number of the apo-ferritin solution used for synthesis, so it can be specifically requested from the manufacturer should additional material need to be purchased. Furthermore, the protein concentration of commercially available apo-ferritin should be stated on the bottle, which can be used to calculate the volume of apo-ferritin solution needed for synthesis. If this is not the case, contact the supplier for this information.
The advantage of gradual addition of metal salts and hydrogen peroxide &#8212; as presented here and in previous reports&#160;&#8212; is that mineralization of the nanoparticle core can be controlled such that different loading factors (i.e., nanoparticle sizes) can be achieved.33 Furthermore, it is possible to purify magnetoferritin further using a magnetic separation column, e.g., a column packed with stainless steel powder secured inside an electromagnet.34 Thus, highly monodisperse nanoparticle cores can be isolated from the bulk magnetoferritin sample. However, for magnetic cell labelling as presented here this is not required. A limitation of magnetoferritin synthesis is the relatively low synthesis yield of about 10%, and the relatively high cost of commercial apo-ferritin solutions. However, apo-ferritin may also be prepared from cheaply available horse spleen ferritin by following established de-mineralization protocols.16
Cationization of magnetoferritin was achieved by adding a molar ratio of 250 molecules of DMPA and 50 molecules of EDC per negatively charged residue (calculations based on the amino acid sequence of horse spleen ferritin). This excess of reagent over protein resulted in high cationization efficiencies, comparable also to previously reported results for the cationization of ferritin.35 For MALDI-TOF analysis, apoferritin and cationized apoferritin were used because of the excessive molecular mass of the magnetoferritin core. To yield high cationization efficiencies, optimal pH is also crucial. EDC-mediated crosslinking is most effective under mildly acidic conditions, and we found that pH 5 yielded optimal cationization results for magnetoferritin. However, for other proteins cationization pH may need to be optimized. Cationization at or close to the isoelectric point of the protein should be avoided, because this may lead to severe precipitation.
Stem cell magnetization with cationized magnetoferritin was highly efficient and could be achieved using incubation times well below 30 minutes. Even a one-minute incubation resulted in a cellular iron content of 3.6 pg, which is within the reported range required to influence T2 and T2* contrast for MRI.36,37 It is also remarkable that this efficient labeling is achieved with low extracellular iron concentrations. For example, previous studies using anionic nanoparticles report iron levels of 10 pg per cell after a 30-minute incubation period with 5 mM iron.38 In comparison, incubation with a cationized magnetoferritin solution containing 0.5 &#956;M protein corresponds to incubation with approximately 0.2 mM iron and also yields approximately 10 pg of iron per cell after 30 minutes. We were not able to clearly identify any endocytotic vesicles using TEM. However, previous studies using cationized ferritin found that internalization occurred within the first ten minutes of exposure.39,40 Cationized ferritin could be localized in coated vesicles, indicating clathrin- or caveolin-dependent endocytosis. The same studies also reported that after 30 minutes of incubation, cationized ferritin was still present on the cell surface, as well as in multivesicular bodies, resembling lysosomes.
Further applications could include cationization of apo-ferritin cages loaded with other nanoparticles and/or functional molecules, such as anti-cancer drugs41 or quantum dots42. Cationization of these ferritin constructs could result in faster and more efficient delivery of their cargo to cells.

Surface binding or internalization of superparamagnetic iron oxide nanoparticles (SPIONs) has enabled magnetization of a variety of cell types for applications such as imaging and remote manipulation.1 However, achieving sufficient cellular magnetization can be a challenge, particularly when the interaction between the SPION and the cell surface is weak.2 In the past, prolonged exposure or high SPION concentrations have been employed as strategies to overcome this challenge.3,4 Nevertheless, these strategies are problematic because they increase toxicity5,6 and have very limited success in cell types with low internalization rates, such as lymphocytes.7 To enhance cellular uptake of SPIONs, several surface functionalization approaches have been explored. For instance, antibodies have been used to promote receptor-mediated endocytosis,8 while non-specific uptake can be achieved using transfection agents9,10 or cell-penetrating species, such as HIV tat-peptide.11,12 However, antibody and peptide functionalization approaches are limited by expensive reagents and complex synthetic preparation, while transfection agents can induce nanoparticle precipitation and adversely affect cell function.13,14 
We recently reported the synthesis of chemically cationized magnetoferritin, a novel SPION which was highly effective in magnetizing human mesenchymal stem cells (hMSCs) using incubation times as short as one minute.15 Magnetoferritin is synthesized by reconstituting a SPION inside the de-mineralized cavity of the iron storage protein ferritin.16 This protein-based SPION combines many properties that make it well suited for cell magnetization, such as control over the magnetic properties of the magnetic core,17-19 and biocompatibility and aqueous solubility conferred by the protein shell. Furthermore, surface functionalization is easily achieved due to addressable amino acids that can be chemically20-22 or genetically modified.23-25 We have shown that chemical cationization of the acidic amino acid residues of the protein shell generates a stable nanoparticle that readily interacted with anionic domains on the cell surface leading to rapid and persistent cell magnetization. This procedure eliminates the need for laborious functionalization and lengthy incubation protocols, and due the non-specific labelling mechanism this rapid magnetization strategy should find wide-spread application in other cell types. Here, we present an in depth report of the ultra-fast cell labeling method, including detailed protocols of the synthesis, purification and surface functionalization of cationized magnetoferritin.

<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td>4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES)</td>
			<td>Fisher Scientific</td>
			<td>BPE310-1</td>
			<td>powder; prepare a 1 M stock solution at pH 8.6 and dilute to 50 mM prior to use. Check the pH carefully prior to synthesis!</td>
		</tr>
		<tr>
			<td>apoferritin from equine spleen</td>
			<td>Sigma Aldrich</td>
			<td>A3641</td>
			<td>we used LOT# 081M7011V</td>
		</tr>
		<tr>
			<td>cobalt sulfate heptahydrate&#160;</td>
			<td>Sigma Aldrich</td>
			<td>C6768</td>
			<td>prepare fresh solutions from the salt prior to synthesis</td>
		</tr>
		<tr>
			<td>ammonium iron sulphate hexahydrate&#160;</td>
			<td>Sigma Aldrich</td>
			<td>F1543</td>
			<td>prepare fresh solutions from the salt prior to synthesis</td>
		</tr>
		<tr>
			<td>hydrogen peroxide solution (30%)</td>
			<td>Sigma Aldrich</td>
			<td>216763</td>
			<td>prepare fresh solutions from the salt prior to synthesis</td>
		</tr>
		<tr>
			<td>sodium citrate</td>
			<td>Sigma Aldrich</td>
			<td>S1804</td>
			<td>powder; a 1 M solution can be prepared and kept at room temperature for several months</td>
		</tr>
		<tr>
			<td>Millex GP filter unit, 0.22 micron</td>
			<td>Merck Millipore</td>
			<td>SLGP033RS</td>
			<td>syringe filter</td>
		</tr>
		<tr>
			<td>Trizma base</td>
			<td>Sigma Aldrich</td>
			<td>T1503</td>
			<td>powder; prepare a 1 M stock solution at pH 8.0 and dilute to 50 mM prior to use</td>
		</tr>
		<tr>
			<td>sodium chloride</td>
			<td>Sigma Aldrich</td>
			<td>31434</td>
			<td>poweder; add to buffers as required</td>
		</tr>
		<tr>
			<td>Centriprep centrifugal filter units</td>
			<td>Merck Millipore</td>
			<td>4310</td>
			<td>Ultracel YM-50 membrane, 12 mL volume; use for initial concentration until the magnetoferritin solution has been concentrated from about 150 mL to 20 mL</td>
		</tr>
		<tr>
			<td>Amicon Ultra-4 centrifugal filter untis</td>
			<td>Merck Millipore</td>
			<td>UFC801024</td>
			<td>Ultracel-10 membrane, 4 mL volume; use to concentrate magnetoferritin solution from about 20 mL to 2 mL</td>
		</tr>
		<tr>
			<td>ANX Sepharose 4 Fast Flow</td>
			<td>GE Healthcare</td>
			<td>17-1287-04</td>
			<td>we packed this column ourselves</td>
		</tr>
		<tr>
			<td>HiPrep 26/60 Sephacryl S-300 HR column&#160;</td>
			<td>GE Healthcare</td>
			<td>17-1196-01</td>
			<td>this column was bought ready packed</td>
		</tr>
		<tr>
			<td>&#196;KTA purifier system</td>
			<td>GE Healthcare</td>
			<td>28406264</td>
			<td></td>
		</tr>
		<tr>
			<td>sample pump P-960</td>
			<td>GE Healthcare</td>
			<td>18-6727-00</td>
			<td>load sample at a flow rate of 10 mL/min</td>
		</tr>
		<tr>
			<td>automated fraction collector Frac-950</td>
			<td>GE Healthcare</td>
			<td>18-6083-00</td>
			<td></td>
		</tr>
		<tr>
			<td>Bradford assay reagent</td>
			<td>Sigma Aldrich</td>
			<td>B6916</td>
			<td>solution ready to use</td>
		</tr>
		<tr>
			<td>Ferritin, Type I: from horse spleen</td>
			<td>Sigma Aldrich</td>
			<td>F4503</td>
			<td>prepare ferritin standards from this solution to determine magnetoferritin concentration</td>
		</tr>
		<tr>
			<td>N,N-dimethyl-1,3-propanediamine (DMPA)</td>
			<td>Sigma Aldrich</td>
			<td>308110</td>
			<td>CAUTION: when adjusting the pH of a DMPA solution, perform this step in a fume hood</td>
		</tr>
		<tr>
			<td>N-(3-dimethylaminopropyl)-N&#8217;-ethylcarbodiimide hydrochloride (EDC)</td>
			<td>Sigma Aldrich</td>
			<td>E6383</td>
			<td>keep in freezer but bring to room temperature before opening the bottle</td>
		</tr>
		<tr>
			<td>&#160;2-(N-morpholino)ethanesulfonic acid (MES)</td>
			<td>AppliChem</td>
			<td>A0689,0500</td>
			<td>powder; prepare a 200 M stock solution at pH 5</td>
		</tr>
		<tr>
			<td>dialysis tubing cellulose membrane</td>
			<td>Sigma Aldrich</td>
			<td>D9652</td>
			<td>soak 10 min in deionized water before use</td>
		</tr>
		<tr>
			<td>Dulbecco&#8217;s Modified Eagle&#8217;s Medium (DMEM), 1000 mg/L glucose</td>
			<td>Sigma Aldrich</td>
			<td>D5546</td>
			<td>warm in 37 &#176;C&#160; water bath before use</td>
		</tr>
		<tr>
			<td>fetal bovine serum</td>
			<td>Sigma Aldrich</td>
			<td>F7524</td>
			<td>add to stock DMEM bottle, 10 % (v/v) final concentration</td>
		</tr>
		<tr>
			<td>penicillin/streptomycin solution</td>
			<td>Sigma Aldrich</td>
			<td>P0781</td>
			<td>add to stock DMEM bottle, 1 % (v/v) final concentration</td>
		</tr>
		<tr>
			<td>glutamax solution</td>
			<td>Gibco</td>
			<td>35050-087</td>
			<td>add to stock DMEM bottle, 1 % (v/v) final concentration</td>
		</tr>
		<tr>
			<td>human fibroblast growth factor</td>
			<td>PeproTech</td>
			<td>100-18B</td>
			<td>add to DMEM freshly into cell culture flask with each media change; final concentration 5 ng/mL</td>
		</tr>
		<tr>
			<td>phosphate buffered saline</td>
			<td>Sigma Aldrich</td>
			<td>D8537</td>
			<td>sterile solution, for cell cultrue</td>
		</tr>
		<tr>
			<td>trypsin/EDTA solution</td>
			<td>Sigma Aldrich</td>
			<td>E5134</td>
			<td>keep in freezer and defrost in 37 &#176;C&#160; water bath before use</td>
		</tr>
		<tr>
			<td>ethylenediaminetetraacetic acid (EDTA)</td>
			<td>Sigma Aldrich</td>
			<td>E5134</td>
			<td>powder; make a 2 mM solution in PBS&#160;</td>
		</tr>
		<tr>
			<td>bovine serum albumin</td>
			<td>Sigma Aldrich</td>
			<td>A7030</td>
			<td>add 0.5 % (w/v) into 2 mM EDTA solution in PBS; carefully stir with magnetic stirrer, avoid foaming; filter sterilize through a 0.22 micron syringe filter</td>
		</tr>
		<tr>
			<td>MACS multi stand&#160;</td>
			<td>Miltenyi Biotec</td>
			<td>130-042-303</td>
			<td>for attachment of MACS magnet</td>
		</tr>
		<tr>
			<td>MACS MS columns</td>
			<td>Miltenyi Biotec</td>
			<td>130-042-201</td>
			<td>disposable; intended for single use, but if sterility is not required, they can re-used: wash with deionized water and 100 % ethanol, and placed in a drying oven; discard if you observe rusty patches</td>
		</tr>
		<tr>
			<td>MiniMACS separator magnet</td>
			<td>Miltenyi Biotec</td>
			<td>130-042-102</td>
			<td>can be bought as a starter kit, together with columns and stands</td>
		</tr>
		<tr>
			<td>MACS column pre-separation filter</td>
			<td>Miltenyi Biotec</td>
			<td>130-041-407</td>
			<td>30 mm filter</td>
		</tr>
		<tr>
			<td>Nitric acid solution, 64-66%</td>
			<td>Sigma Aldrich</td>
			<td>7006</td>
			<td></td>
		</tr>
		<tr>
			<td>Titrando 907, syringe pump</td>
			<td>Metrohm</td>
			<td>2.907.0020</td>
			<td></td>
		</tr>
		<tr>
			<td></td>
			<td></td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td colspan="2">Equipment used to characterize magnetoferritin and cationized magnetoferritin</td>
			<td></td>
			<td></td>
		</tr>
		<tr>
			<td>SpectraMax M5</td>
			<td>Molecular Devices</td>
			<td></td>
			<td>Used to measure absorbance in the Bradford assay</td>
		</tr>
		<tr>
			<td>JEM 1200 EX</td>
			<td>JEOL</td>
			<td></td>
			<td>Used for TEM imaging of magnetoferritin</td>
		</tr>
		<tr>
			<td>InVia Raman spectrometer</td>
			<td>Renishaw</td>
			<td></td>
			<td>Used for Raman spectroscopy</td>
		</tr>
		<tr>
			<td>Torus DPSS laser</td>
			<td>Laser Quantum</td>
			<td></td>
			<td>Used for Raman spectroscopy</td>
		</tr>
		<tr>
			<td>Bruker UltrafleXtreme</td>
			<td>Applied Biosystems</td>
			<td></td>
			<td>Used for MALDI-TOF analysis of apoferritin and cationized apoferritin</td>
		</tr>
		<tr>
			<td>ZetaSizer Nano-ZS</td>
			<td>Malvern Instruments</td>
			<td></td>
			<td>Used to measure hydrodynamic diameter and zeta potential of magnetoferritin and cationized magnetoferritin</td>
		</tr>
		<tr>
			<td>Magnetic Property Measurement System</td>
			<td>Quantum Design</td>
			<td></td>
			<td>Used to measure magnetic saturation moment and magnetic susceptibility</td>
		</tr>
		<tr>
			<td>Magnetom Skyra</td>
			<td>Siemens</td>
			<td></td>
			<td>Used to determine longitudinal and transverse relaxivity&#160;</td>
		</tr>
		<tr>
			<td>Tecnai 12 BioTwin Spirit</td>
			<td>FEI</td>
			<td></td>
			<td>Used for TEM imaging of hMSC labeled with cationized magnetoferritin</td>
		</tr>
		<tr>
			<td>710 ICP-OES</td>
			<td>Agilent</td>
			<td></td>
			<td>Used to determine iron content in cells</td>
		</tr>
	</tbody>
</table>

synthesis of cationized magnetoferritin for ultra-fast magnetization of cells

Many important biomedical applications, such as cell imaging and remote manipulation, can be achieved by labeling cells with superparamagnetic iron oxide nanoparticles (SPIONs). Achieving sufficient cellular uptake of SPIONs is a challenge that has traditionally been met by exposing cells to elevated concentrations of SPIONs or by prolonging exposure times (up to 72 hr). However, these strategies are likely to mediate toxicity. Here, we present the synthesis of the protein-based SPION magnetoferritin as well as a facile surface functionalization protocol that enables rapid cell magnetization using low exposure concentrations. The SPION core of magnetoferritin consists of cobalt-doped iron oxide with an average particle diameter of 8.2 nm mineralized inside the cavity of horse spleen apo-ferritin. Chemical cationization of magnetoferritin produced a novel, highly membrane-active SPION that magnetized human mesenchymal stem cells (hMSCs) using incubation times as short as one minute and iron concentrations as lows as 0.2 mM.

TEM was used to confirm nanoparticle mineralization inside the apoferritin cavity and determine the average core size (Figures 1A and 1B). Image analysis of unstained magnetoferritin samples gave an average core diameter of 8.2 &#177; 0.7 nm, and aurothioglucose stain confirmed the presence of nanoparticles within the protein cage. Note that the images show a magnetoferritin sample that was further purified using magnetic separation to isolate uniform nanoparticle cores. Magnetoferritin samples that were not magnetically purified have a slightly broader core size distribution.29 Analysis of the structure of the magnetoferritin core using selected-area electron diffraction indicated the possible presence of the inverse spinel structure based on magnetite (Fe3O4) and/or maghemite (&#947;-Fe2O3), as well as the spinel structure due to Co3O4. Furthermore, Raman spectra revealed peaks attributed to Fe3O4, small amounts of &#947;-Fe2O3, and a cobalt ferrite (Figure 1 C). ICP-OES analysis of magnetoferritin showed an average of 102 &#956;g of iron and 0.9 &#956;g of cobalt per milligram of magnetoferritin.
A schematic is included, illustrating the subsequent cationization step (Figure 2 A). The hydrodynamic diameter of magnetoferritin and cationized magnetoferritin was 11.8 &#177; 1.1 nm and 12.5 &#177; 1.4 nm, respectively, as determined by dynamic light scattering. The cationization efficiency of covalent DMPA-coupling to magnetoferritin was assessed using zeta potentiometry and matrix-assisted laser desorption ionization time-of-flight (MALDI-TOF) mass spectrometry. The zeta potential changed from -10.5 mV for MF to + 8.3 mV for cationized magnetoferritin, confirming a change in surface potential from negative to positive (Table 1). Mass spectrometry experiments found a subunit molecular weight of 20.1 kDa for native apo-ferritin and 21.1 kDa for cationized apo-ferritin (Figure 2 B). This mass increase corresponds to approximately 12 coupled DMPA molecules per protein subunit, and the cationization of 288 residues on the entire 24-subunit protein.
Magnetic saturation and susceptibility were measured using SQUID magnetometry, and transverse and longitudinal relaxivity were measured using magnetic resonance imaging. Magnetic properties were similar for magnetoferritin and cationized magnetoferritin, indicating that cationization had negligible impact on the magnetic properties of the enclosed SPION (Table 1). Furthermore, these properties are similar to other iron oxide based nanoparticles,19,30 demonstrating that cationized magnetoferritin would be as suitable as conventional SPION-based MRI contrast agents in enhancing imaging contrast.
After a 30-minute exposure, the cell surface was densely covered with cationized magnetoferritin (Figure 3 A). However, after one week, no nanoparticles were found on the cell surface (Figure 3 B). Cationized magnetoferritin was remarkably effective at magnetically labelling hMSCs. Notably, exposing the cells to cationized magnetoferritin for one minute resulted in the magnetization of 92% of the cell population and the delivery of 3.6 pg of iron per cell. Increasing the incubation time to 15 minutes resulted in the magnetization of the entire cell population (Figure 3 C).
<img alt="Figure 1" src="/files/ftp_upload/54785/54785fig1.jpg" /> 
Figure 1: Characterization of magnetoferritin cores doped with 5% cobalt. TEM images of magnetoferritin stained with aurothioglucose (A) and unstained (B). Inset shows corresponding electron diffraction with magnetite indices. Scale bar: 20 nm. (C) Raman spectrum for magnetoferritin. The arrows indicate the main Raman vibration modes for cobalt ferrite (T2g), magnetite and maghemite (both A1g).31,32 The laser wavelength used was 532 nm. (Image adapted from Okuda et al.18). Note that this magnetoferritin sample had been further purified using magnetic separation, which isolated uniformly loaded magnetoferritin particles. <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/54785/54785fig1large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 2" src="/files/ftp_upload/54785/54785fig2.jpg" /> 
Figure 2: Cationization of magnetoferritin. A) Solvent accessible surface area representations showing the distribution of acidic (red) and basic (yellow) amino acid residues on the protein surface. Magnetoferritin (1) is modified to cationized magnetoferritin (2) by carbodiimide-mediated crosslinking of DMPA to acidic amino acid residues on the protein surface (3). B) Mass spectrometry analysis of apo-ferritin and cationized apo-ferritin subunits. Mass-to-charge (m/z) spectrum of apoferritin (ApoF) and cationized apoferritin (cat-ApoF) generated by MALDI-TOF. A mass increase from 20.1 kDa to 21.1 kDa is observed after cationization. (Image adapted from Correia Carreira et al.15) <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/54785/54785fig2large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<img alt="Figure 3" src="/files/ftp_upload/54785/54785fig3.jpg" /> 
Figure 3: Magnetic labeling and cell separation of hMSCs incubated with cationized magnetoferritin. A) TEM image of hMSCs after a 30-minute incubation with cationized magnetoferritin. The arrow indicates the presence of magnetoferritin cores densely packed on the cell surface. Scale bars: 200 nm. B) TEM image of hMSC one week after labeling. The cell surface is clear of cationized magnetoferritin. C) Investigating the rapidity of magnetic labeling: 92% of the cell population were magnetized after a one-minute exposure with 0.5 &#956;M cationized magnetoferritin, and the entire cell population was magnetized within 15 minutes. Iron content per cell was determined using ICP-OES. Average and standard deviation from three biological replicates are shown. (Image adapted from Correia Carreira et al.15) <a href="https://cloudflare-jove-com.remotexs.ntu.edu.sg/files/ftp_upload/54785/54785fig3large.jpg" target="_blank">Please click here to view a larger version of this figure.</a>
<table border="1" fo:keep-together.within-page="1" fo:keep-with-next.within-page="always">
	<tbody>
		<tr>
			<td></td>
			<td>MF</td>
			<td>cat-MF</td>
		</tr>
		<tr>
			<td>Hydrodynamic diameter [nm]</td>
			<td>11.8 &#177; 1.1</td>
			<td>12.5 &#177; 1.4</td>
		</tr>
		<tr>
			<td>Zeta potential [mv]</td>
			<td>(-)10.4 &#177; 0.2</td>
			<td>8.3 &#177; 0.7</td>
		</tr>
		<tr>
			<td>Magnetic saturation moment [Am2 kg-1]</td>
			<td>54.9 &#177; 1.6</td>
			<td>55.3 &#177; 1.4</td>
		</tr>
		<tr>
			<td>Mass susceptibility [x 104 m3 kg-1]</td>
			<td>1.75 &#177; 0.08</td>
			<td>1.75&#177; 0.07</td>
		</tr>
		<tr>
			<td>Longitudinal relaxivity [mM-1 sec-1]</td>
			<td>2.6 &#177; 0.1</td>
			<td>2.3 &#177; 0.1</td>
		</tr>
		<tr>
			<td>Transverse relaxivity [mM-1 sec-1]</td>
			<td>44.6 &#177; 1.0</td>
			<td>52.8 &#177; 0.8</td>
		</tr>
	</tbody>
</table>
Table 1: Physicochemical characterization of magnetoferritin (MF) and cationized magnetoferritin (cat-MF). (Table adapted from Correia Carreira et al.15)

Watch this Scientific Journal Video about Synthesis of Cationized Magnetoferritin for Ultra-fast Magnetization of Cells at JoVE.com

Synthesis of Cationized Magnetoferritin for Ultra-fast Magnetization of Cells

A protocol for the synthesis and cationization of cobalt-doped magnetoferritin is presented, as well as a method to rapidly magnetize stem cells with cationized magnetoferritin.

Many important biomedical applications, such as cell imaging and remote manipulation, can be achieved by labeling cells with superparamagnetic iron oxide ...

synthesis-cationized-magnetoferritin-for-ultra-fast-magnetization

Nanyang Technological University

Research

JoVE Journal

Bioengineering

9.9K Views.  University of Bristol. A protocol for the synthesis and cationization of cobalt-doped magnetoferritin is presented, as well as a method to rapidly magnetize stem cells with cationized magnetoferritin.

Video: Synthesis of Cationized Magnetoferritin for Ultra-fast Magnetization of Cells

Synthesis, Assembly, and Characterization of Monolayer Protected Gold Nanoparticle Films for Protein Monolayer Electrochemistry

Colloidal gold nanoparticles protected with alkanethiolate ligands called monolayer protected gold clusters (MPCs) are synthesized and subsequently incorporated into film assemblies that serve as adsorption platforms for protein monolayer electrochemistry (PME). PME is utilized as the model system for studying electrochemical properties of redox proteins by confining them to an adsorption platform at a modified electrode, which also serves as a redox partner for electron transfer (ET) reactions. Studies have shown that gold nanoparticle film assemblies of this nature provide for a more homogeneous protein adsorption environment and promote ET without distance dependence compared to the more traditional systems modified with alkanethiol self-assembled monolayers (SAM).1-3 In this paper, MPCs functionalized with hexanethiolate ligands are synthesized using a modified Brust reaction4 and characterized with ultraviolet visible (UV-Vis) spectroscopy, transmission electron microscopy (TEM), and proton (1H) nuclear magnetic resonance (NMR). MPC films are assembled on SAM modified gold electrode interfaces by using a "dip cycle" method of alternating MPC layers and dithiol linking molecules. Film growth at gold electrode is tracked electrochemically by measuring changes to the double layer charging current of the system. Analogous films assembled on silane modified glass slides allow for optical monitoring of film growth and cross-sectional TEM analysis provides an estimated film thickness. During film assembly, manipulation of the MPC ligand protection as well as the interparticle linkage mechanism allow for networked films, that are readily adaptable, to interface with redox protein having different adsorption mechanism. For example, Pseudomonas aeruginosa azurin (AZ) can be adsorbed hydrophobically to dithiol-linked films of hexanethiolate MPCs and cytochrome c (cyt c) can be immobilized electrostatically at a carboxylic acid modified MPC interfacial layer. In this report, we focus on the film protocol for the AZ system exclusively. Investigations involving the adsorption of proteins on MPC modified synthetic platforms could further the understanding of interactions between biomolecules and man-made materials, and consequently aid the development of biosensor schemes, ET modeling systems, and synthetic biocompatible materials.5-8

Alkanethiolate stabilized gold colloids known as monolayer protected clusters (MPCs) are synthesized, characterized, and assembled into thin films as an adsorption interface for protein monolayer electrochemistry of simple redox protein like Pseudomonas aeruginosa azurin (AZ) and cytochrome c (cyt c).

Colloidal gold nanoparticles protected with alkanethiolate ligands called monolayer protected gold clusters (MPCs) are synthesized and subsequently ...

Transplantation of Induced Pluripotent Stem Cell-derived Mesoangioblast-like Myogenic Progenitors in Mouse Models of Muscle Regeneration

Patient-derived iPSCs could be an invaluable source of cells for future autologous cell therapy protocols. iPSC-derived myogenic stem/progenitor cells similar to pericyte-derived mesoangioblasts (iPSC-derived mesoangioblast-like stem/progenitor cells: IDEMs) can be established from iPSCs generated from patients affected by different forms of muscular dystrophy. Patient-specific IDEMs can be genetically corrected with different strategies (e.g. lentiviral vectors, human artificial chromosomes) and enhanced in their myogenic differentiation potential upon overexpression of the myogenesis regulator MyoD. This myogenic potential is then assessed in vitro with specific differentiation assays and analyzed by immunofluorescence. The regenerative potential of IDEMs is further evaluated in vivo, upon intramuscular and intra-arterial transplantation in two representative mouse models displaying acute and chronic muscle regeneration. The contribution of IDEMs to the host skeletal muscle is then confirmed by different functional tests in transplanted mice. In particular, the amelioration of the motor capacity of the animals is studied with treadmill tests. Cell engraftment and differentiation are then assessed by a number of histological and immunofluorescence assays on transplanted muscles. Overall, this paper describes the assays and tools currently utilized to evaluate the differentiation capacity of IDEMs, focusing on the transplantation methods and subsequent outcome measures to analyze the efficacy of cell transplantation.

Induced pluripotent stem cell (iPSC)-derived myogenic progenitors are promising candidates for cell therapy strategies to treat muscular dystrophies. This protocol describes transplantation and functional measurements required to evaluate the engraftment and differentiation of iPSC-derived mesoangioblasts (a type of muscle progenitors) in mouse models of acute and chronic muscle regeneration.

Patient-derived iPSCs could be an invaluable source of cells for future autologous cell therapy protocols. iPSC-derived myogenic stem/progenitor cells ...

Synthesis of Keratin-based Nanofiber for Biomedical Engineering

Electrospinning, due to its versatility and potential for applications in various fields, is being frequently used to fabricate nanofibers. Production of these porous nanofibers is of great interest due to their unique physiochemical properties. Here we elaborate on the fabrication of keratin containing poly (&#949;-caprolactone) (PCL) nanofibers (i.e., PCL/keratin composite fiber). Water soluble keratin was first extracted from human hair and mixed with PCL in different ratios. The blended solution of PCL/keratin was transformed into nanofibrous membranes using a laboratory designed electrospinning set up. Fiber morphology and mechanical properties of the obtained nanofiber were observed and measured using scanning electron microscopy and tensile tester. Furthermore, degradability and chemical properties of the nanofiber were studied by FTIR. SEM images showed uniform surface morphology for PCL/keratin fibers of different compositions. These PCL/keratin fibers also showed excellent mechanical properties such as Young&#39;s modulus and failure point. Fibroblast cells were able to attach and proliferate thus proving good cell viability. Based on the characteristics discussed above, we can strongly argue that the blended nanofibers of natural and synthetic polymers can represent an excellent development of composite materials that can be used for different biomedical applications.

Electrospun nanofibers have a high surface area to weight ratio, excellent mechanical integrity, and support cell growth and proliferation. These nanofibers have a wide range of biomedical applications. Here we fabricate keratin/ PCL nanofibers, using the electrospinning technique, and characterize the fibers for possible applications in tissue engineering.

Electrospinning, due to its versatility and potential for applications in various fields, is being frequently used to fabricate nanofibers. Production of ...

Microwave-driven Synthesis of Iron Oxide Nanoparticles for Fast Detection of Atherosclerosis

A fast and reproducible microwave-driven protocol has been developed for the synthesis of neridronate-functionalized nanoparticles. Starting from the synthesis of hydrophobic nanoparticles, our method is based on an adaptation from thermal decomposition method to microwave driven synthesis. The new methodology produces a decrease in the reaction times in comparison with traditional procedures. Moreover, the use of the microwave technology increases the reproducibility of the reactions, something important from the point of view of clinical applications. The novelty of this iron oxide nanoparticle is the attachment of Neridronate. The use of this molecule leads a bisphosphonate moiety towards the outside of the nanoparticle that provides Ca2+ binding properties in vitro and selective accumulation in vivo in the atheroma plaque. The protocol allows the synthesis and plaque detection in about 3 hr since the initial synthesis from organic precursors. Their accumulation in the atherosclerotic area in less than 1 hr provides a contrast agent particularly suitable for clinical applications.

Microwave technology enables extremely fast synthesis of iron oxide nanoparticles for atherosclerosis plaque characterization. The use of an aminobisphosphonate in the external side of the nanoparticle provides a fast accumulation in the atherosclerotic area.

A fast and reproducible microwave-driven protocol has been developed for the synthesis of neridronate-functionalized nanoparticles. Starting from the ...

The Synthesis of RGD-functionalized Hydrogels as a Tool for Therapeutic Applications

The use of polymers as biomaterials has provided significant advantages in therapeutic applications. In particular, the possibility to modify and functionalize polymer chains with compounds that are able to improve biocompatibility, mechanical properties, or cell viability allows the design of novel materials to meet new challenges in the biomedical field. With the polymer functionalization strategies, click chemistry is a powerful tool to improve cell-compatibility and drug delivery properties of polymeric devices. Similarly, the fundamental need of biomedicine to use sterile tools to avoid potential adverse-side effects, such as toxicity or contamination of the biological environment, gives rise to increasing interest in the microwave-assisted strategy.
The combination of click chemistry and the microwave-assisted method is suitable to produce biocompatible hydrogels with desired functionalities and improved performances in biomedical applications. This work aims to synthesize RGD-functionalized hydrogels. RGD (arginylglycylaspartic acid) is a tripeptide that can mimic cell adhesion proteins and bind to cell-surface receptors, creating a hospitable microenvironment for cells within the 3D polymeric network of the hydrogels. RGD functionalization occurs through Huisgen 1,3-dipolar cycloaddition. Some PAA carboxyl groups are modified with an alkyne moiety, whereas RGD is functionalized with azido acid as the terminal residue of the peptide sequence. Finally, both products are used in a copper catalyzed click reaction to permanently link the peptide to PAA. This modified polymer is used with carbomer, agarose and polyethylene glycol (PEG) to synthesize a hydrogel matrix. The 3D structure is formed due to an esterification reaction involving carboxyl groups from PAA and carbomer and hydroxyl groups from agarose and PEG through microwave-assisted polycondensation. The efficiency of the gelation mechanism ensures a high degree of RGD functionalization. In addition, the procedure to load therapeutic compounds or biological tools within this functionalized network is very simple and reproducible.

We present a protocol for the synthesis of RGD-functionalized hydrogels as devices for cell and drug delivery. The procedure involves copper catalyzed alkyne-azide cycloaddition (CuAAC) between alkyne-modified polyacrylic acid (PAA) and a RGD-azide derivative. The hydrogels are formed using microwave-assisted polycondensation and their physicochemical properties are investigated.

The use of polymers as biomaterials has provided significant advantages in therapeutic applications. In particular, the possibility to modify and ...

Synthesis of Hydrogels with Antifouling Properties As Membranes for Water Purification

Hydrogels have been widely utilized to enhance the surface hydrophilicity of membranes for water purification, increasing the antifouling properties and thus achieving stable water permeability through membranes over time. Here, we report a facile method to prepare hydrogels based on zwitterions for membrane applications. Freestanding films can be prepared from sulfobetaine methacrylate (SBMA) with a crosslinker of poly(ethylene glycol) diacrylate (PEGDA) via photopolymerization. The hydrogels can also be prepared by impregnation into hydrophobic porous supports to enhance the mechanical strength. These films can be characterized by attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) to determine the degree of conversion of the (meth)acrylate groups, using goniometers for hydrophilicity and differential scanning calorimetry (DSC) for polymer chain dynamics. We also report protocols to determine the water permeability in dead-end filtration systems and the effect of foulants (bovine serum albumin, BSA) on membrane performance.

This paper reports practical methods to prepare hydrogels in freestanding films and impregnated membranes and to characterize their physical properties, including water transport properties.

Hydrogels have been widely utilized to enhance the surface hydrophilicity of membranes for water purification, increasing the antifouling properties and ...

Synthesis of Monocyte-targeting Peptide Amphiphile Micelles for Imaging of Atherosclerosis

Atherosclerosis is a major contributor to cardiovascular disease, the leading cause of death worldwide, which claims 17.3 million lives annually. Atherosclerosis is also the leading cause of sudden death and myocardial infarction, instigated by unstable plaques that rupture and occlude the blood vessel without warning. Current imaging modalities cannot differentiate between stable and unstable plaques that rupture. Peptide amphiphiles micelles (PAMs) can overcome this drawback as they can be modified with a variety of targeting moieties that bind specifically to diseased tissue. Monocytes have been shown to be early markers of atherosclerosis, while large accumulation of monocytes is associated with plaques prone to rupture. Hence, nanoparticles that can target monocytes can be used to discriminate different stages of atherosclerosis. To that end, here, we describe a protocol for the preparation of monocyte-targeting PAMs (monocyte chemoattractant protein-1 (MCP-1) PAMs). MCP-1 PAMs are self-assembled through synthesis under mild conditions to form nanoparticles of 15 nm in diameter with near neutral surface charge. In vitro, PAMs were found to be biocompatible and had a high binding affinity for monocytes. The methods described herein show promise for a wide range of applications in atherosclerosis as well as other inflammatory diseases.

This paper presents a method involving the synthesis and characterization of monocyte-targeting peptide amphiphile micelles and the corresponding assays to test for biocompatibility and ability of the micelle to bind to monocytes.

Atherosclerosis is a major contributor to cardiovascular disease, the leading cause of death worldwide, which claims 17.3 million lives annually. ...

Design and Synthesis of a Reconfigurable DNA Accordion Rack

DNA nanostructure-based mechanical systems or DNA nanomachines, which produce complex nanoscale motion in 2D and 3D in the nanometer to &#229;ngstr&#246;m resolution, show great potential in various fields of nanotechnology such as the molecular reactors, drug delivery, and nanoplasmonic systems. The reconfigurable DNA accordion rack, which can collectively manipulate a 2D or 3D nanoscale network of elements, in multiple stages in response to the DNA inputs, is described. The platform has potential to increase the number of elements that DNA nanomachines can control from a few elements to a network scale with multiple stages of reconfiguration.
In this protocol, we describe the entire experimental process of the reconfigurable DNA accordion rack of 6 by 6 meshes. The protocol includes a design rule and simulation procedure of the structures and a wet-lab experiment for synthesis and reconfiguration. In addition, analysis of the structure using TEM (transmission electron microscopy) and FRET (fluorescence resonance energy transfer) is included in the protocol. The novel design and simulation methods covered in this protocol will assist researchers to use the DNA accordion rack for further applications.

We describe the detailed protocol for design, simulation, wet-lab experiments, and analysis for a reconfigurable DNA accordion rack of 6 by 6 meshes.

DNA nanostructure-based mechanical systems or DNA nanomachines, which produce complex nanoscale motion in 2D and 3D in the nanometer to &#229;ngstr&#246;m ...

In Vesiculo Synthesis of Peptide Membrane Precursors for Autonomous Vesicle Growth

Compartmentalization of biochemical reactions is a central aspect of synthetic cells. For this purpose, peptide-based reaction compartments serve as an attractive alternative to liposomes or fatty acid-based vesicles. Externally or within the vesicles, peptides can be easily expressed and simplify the synthesis of membrane precursors. Provided here is a protocol for the creation of vesicles with diameters of ~200 nm based on the amphiphilic elastin-like polypeptides (ELP) utilizing dehydration-rehydration from glass beads. Also presented are protocols for bacterial ELP expression and purification via inverse temperature cycling, as well as their covalent functionalization with fluorescent dyes. Furthermore, this report describes a protocol to enable the transcription of RNA aptamer dBroccoli inside ELP vesicles as a less complex example for a biochemical reaction. Finally, a protocol is provided, which allows in vesiculo expression of fluorescent proteins and the membrane peptide, whereas synthesis of the latter results in vesicle growth.

Presented here are protocols for the creation of peptide-based small unilamellar vesicles capable of growth. To facilitate in vesiculo production of the membrane peptide, these vesicles are equipped with a transcription-translation system and the peptide-encoding plasmid.

Compartmentalization of biochemical reactions is a central aspect of synthetic cells. For this purpose, peptide-based reaction compartments serve as an ...

Synthesis of Near-Infrared Emitting Gold Nanoclusters for Biological Applications

Over the past decade, fluorescent gold nanoclusters (AuNCs) have witnessed growing popularity in biological applications and enormous efforts have been devoted to their development. In this protocol, a recently developed, facile method for preparation of water soluble, biocompatible, and colloidally stable near-infrared emitting AuNCs have been described in detail. This room-temperature, bottom-up chemical synthesis provides easily functionalizable AuNCs capped with thioctic acid and thiol-modified polyethylene glycol in aqueous solution. The synthetic approach requires neither organic solvents or additional ligand exchange nor extensive knowledge of synthetic chemistry to reproduce. The resulting AuNCs offer free surface carboxylic acids, which can be functionalized with various biological molecules bearing a free amine group without adversely affecting the photoluminescent properties of the AuNCs. A quick, reliable procedure for flow cytometric quantification and confocal microscopic imaging of AuNC uptake by HeLa cells also been described. Due to the large Stokes shift, proper setting of filters in flow cytometry and confocal microscopy is necessary for efficient detection of near-infrared photoluminescence of AuNCs.

A reliable and easily reproducible method for preparation of functionalizable, near-infrared emitting photoluminescent gold nanoclusters and their direct detection inside HeLa cells by flow cytometry and confocal laser scanning microscopy is described.

Over the past decade, fluorescent gold nanoclusters (AuNCs) have witnessed growing popularity in biological applications and enormous efforts have been ...