Low-energy Cathodoluminescence for (Oxy)Nitride Phosphors

Nitride and oxynitride (Sialon) phosphors are good candidates for the ultraviolet and visible emission applications. High performance, good stability and ...

National Institute for Materials Science (NIMS)

In this contribution, we propose to combine both narrow-band green (β-sialon:Eu(2+)) and red (K(2)SiF(6):Mn(4+)) phosphors with a blue InGaN chip to achieve white light-emitting diodes (wLEDs) with a large color gamut and a high efficiency for use as the liquid crystal display (LCD) backlighting. β-sialon:Eu(2+), prepared by a gas-pressure sinteing technique, has a peak emission at 535 nm, a full width at half maximum (FWHM) of 54 nm, and an external quantum efficiency of 54.0% under the 450 nm excitation. K(2)SiF(6):Mn(4+) was synthesized by a twe-step co-precipitation methods, and exhibits a sharp line emission spectrum with the most intensified peak at 631 nm, a FWHM of ~3 nm, and an external quantum efficiency of 54.5%. The prepared three-band wLEDs have a high color temperature of 11,184 - 13,769 K (i.e., 7,828 - 8,611 K for LCD displays), and a luminous efficacy of 91 - 96 lm/W, measured under an applied current of 120 mA. The color gamut defined in the CIE 1931 and CIE 1976 color spaces are 85.5 - 85.9% and 94.3 - 96.2% of the NTSC stanadard, respectively. These optical properties are better than those phosphor-cpnverted wLED backlights using wide-band green or red phosphoprs, suggesting that the two narrow-band phosphors investigated are the most suitable luminescent materials for achieving more bright and vivid displays.

Kohsei Takahashi

Sialon Unit

National Institute for Materials Science (NIMS)

Low-energy Cathodoluminescence for (Oxy)Nitride Phosphors

Kohsei Takahashi

.css-o250i3{font-size:18px;font-family:Open Sans,sans-serif;line-height:21.6px;}Sialon Unit

National Institute for Materials Science (NIMS)

Low-energy Cathodoluminescence for (Oxy)Nitride Phosphors

Sialon Unit